Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores
نویسندگان
چکیده مقاله:
A simple method for fabrication of highly ordered gold nanorod film is introduced in this article. The procedure is based on thermal evaporation of gold into a porous anodic alumina film (PAA). The PPA film was fabricated by combining the hard and mild anodization. This combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with controlled pore diameter and length. It was found that gold nanorods configuration affected by the porous anodic alumina film structure such as pore diameter and length. Furthermore the evaporation process change the rods diameter along the nanopores via the decreasing the pore mouth during the gold deposition.
منابع مشابه
fabrication of highly ordered gold nanorods film using alumina nanopores
a simple method for fabrication of highly ordered gold nanorod film is introduced in this article. the procedure is based on thermal evaporation of gold into a porous anodic alumina film (paa). the ppa film was fabricated by combining the hard and mild anodization. this combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with control...
متن کاملFabrication of Ordered Arrays of Nanodots Using Porous Alumina Thin Film Templates
Nanostructured materials have attracted much research over the recent years, as they provide the critical building blocks for the booming of nanoscience and nanotechnology. Nanostructures have novel properties due to the interplay between the size confinement of electrons in small structures and proximity effects. This is relevant for example in device miniaturization towards the Tbit/in record...
متن کاملFabrication of Porous Anodic Alumina with Ultrasmall Nanopores
Anodization of Al foil under low voltages of 1-10 V was conducted to obtain porous anodic aluminas (PAAs) with ultrasmall nanopores. Regular nanopore arrays with pore diameter 6-10 nm were realized in four different electrolytes under 0-30°C according to the AFM, FESEM, TEM images and current evolution curves. It is found that the pore diameter and interpore distance, as well as the barrier lay...
متن کاملFabrication of porous silicon by metal-assisted etching using highly ordered gold nanoparticle arrays
A simple method for the fabrication of porous silicon (Si) by metal-assisted etching was developed using gold nanoparticles as catalytic sites. The etching masks were prepared by spin-coating of colloidal gold nanoparticles onto Si. An appropriate functionalization of the gold nanoparticle surface prior to the deposition step enabled the formation of quasi-hexagonally ordered arrays by self-ass...
متن کاملFabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition
Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morph...
متن کاملCold-welding fabrication of highly ordered gold nanochannel monolayers in aqueous medium.
Herein, we demonstrate that galvanic replacement reaction over aligned Ag nanowire arrays can be employed as a simple and powerful cold-welding technique for large-scale fabrication of highly ordered Au nanochannel monolayers.
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 2 شماره 2
صفحات 235- 240
تاریخ انتشار 2012-06-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023