In this paper we present results of a study on the yttrium doping in lead tungstate crystals. The crystal growth by modified Bridgman method is described. Results of trace analysis on raw materials and crystals are presented. The segregation coefficient of yttrium ions in lead tungstate crystals was determined. The scintillation emission and longitudinal transmittance spectra, light output, dec...

In this paper we present results of a study on the yttrium doping in lead tungstate crystals. The crystal growth by modified Bridgman method is described. Results of trace analysis on raw materials and crystals are presented. The segregation coefficient of yttrium ions in lead tungstate crystals was determined. The scintillation emission and longitudinal transmittance spectra, light output, dec...

High-resolution transmission electron microscopy (HRTEM) employing focus-variation phase-reconstruction methods is used to image the atomic structure of grain boundaries in a silicon nitride ceramic at subangstrom resolution. Complementary energy-dispersive X-ray emission spectroscopy experiments revealed the presence of yttrium ions segregated to the 0.5–0.7-nm thin amorphous boundary layers t...

This work explores the room temperature random stimulated emission at 1.064 μm of a Nd:YAG crystal powder (Neodymium-doped yttrium aluminum garnet) in a very simple pump configuration with no assistance from an internal mirror. The laser threshold energy as a function of pump beam area and pump wavelength has been measured, as well as the temporal dynamics of emission pulses. The absolute energ...

Single-phase phosphors that emit broadband white-light are needed for white-light-emitting diodes (wLEDs) to reach their full potential. However, it is challenging achieve broad emission from single-phase materials. Consequently, polycrystalline inorganic bulk compounds sans doping rare. We report on a well-known garnet compound, i.e., yttrium iron (YIG), without activator-ion doping. Upon near...

Enhanced upconversion (UC) emission was experimentally demonstrated using gold double antenna nanoparticles coupled to nanoslits in gold films. The transmitted red emission from UC ytterbium and erbium co-doped sodium yttrium fluoride (NaYF4:Yb(3+)/Er(3+)) nanoparticles (UC NPs) at ∼665 nm (excited with a 980 nm diode laser) was enhanced relative to the green emission at ∼550 nm. The relatively...

We report a late-time “fireworks-like” particle emission from laser-produced graphite plasma during its evolution. Plasmas were produced using graphite targets excited with 1064 nm Nd: yttrium aluminum garnet (YAG) laser in vacuum. The time evolution of graphite plasma was investigated using fast gated imaging and visible emission spectroscopy. The emission dynamics of plasma is rapidly changin...

A multi–layer gadolinium–doped yttrium oxide thin film was deposited in a combinatorial fashion on a Si (001) substrate using radio–frequency magnetron sputtering. Alternating layers of Y2O3 and Gd were deposited for a total of 9 layers. The film was homogenized in composition by an 850 C 12 hour thermal treatment producing a range of composition from Y1.96Gd0.04O3 – Y1.54Gd0.46O3 in a single f...

The surface plasmons that are enabled by grating coupling in two-dimensional gold nano-particle arrays (AuNPAs) affected the spectral characteristics of the up-conversion (UC) emission from Yb(3+)-Er(3+)-Gd(3+) co-doped sodium yttrium fluoride (NaYF4:Yb/Er/Gd) nano-rods. The red emission of NaYF4:Yb/Er/Gd nano-rods at 660 nm (excited with a 980 nm diode laser) was significantly enhanced by the ...

 Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...