In this work, we demonstrate a novel carrier transporting combination made of tungsten trioxide (WO3) nanomaterials and Cs2CO3/PCBM buffer bilayer for the fabrication of perovskite solar cells (PSCs). Two different types of WO3, including nanoparticles and nanorods, were prepared by sol-gel process and hydrothermal method, respectively. Cs2CO3/PCBM buffer bilayer was inserted between WO3 and pe...

Ultrafine WO3 nanoparticles were synthesized by nanocasting route, using mesoporous SiO2 as a template. BET measurements showed a specific surface area of 700 m 2/gr for synthesized SiO2, while after impregnation and template removal, this area was reduced to 43 m 2/gr for WO3 nanoparticles. HRTEM results showed single crystalline nanoparticles with average particle size of about 5 nm possessin...

two facile and low cost routes were used for the synthesis of if-ws2 nanoparticles. in this paper, preparation of if-ws2 nanoparticles with two different methods was investigated. in the first method, wo3 nanoparticles were reacted with h2s gas in n2/h2 reducing atmosphere at 900 oc. the as-synthesized if-ws2 nanoparticles are spherical shape with an average size of about 70 nm.  in the second ...

Photothermal therapy, as a physical therapeutic technique to kill cancer, has generated a great deal of interest. Photothermal agents hence play a critical role in this modern therapy. We report the use of transition metal oxides as photothermal agents based on PEGylated WO3-x nanoparticles. The well-prepared nanoparticles presented effective results during photothermal therapy both in vitro an...

tungsten trioxide nanoparticles with two different sizes (average particle sizes about 50 and 80 nm) were prepared by the spray pyrolysis method. photo degradation of congo red (azo dye) showed that photo catalytic property of the as-prepared wo3 nanoparticles with average size about 80 nm is higher than the sample with average size about 50 nm. photo degradation of rhodamine b (cationic triary...

A highly efficient and stable QLED using an inorganic WO3 nanoparticle film as a hole injection layer is demonstrated.The resulting WO3 nanoparticle-based QLEDs also exhibit superior performance compared to that of the present PEDOT:PSS-based QLEDs. The results indicate that WO3 nanoparticles are promising solution-processed buffer layer materials and serve as a strong candidate for QLED techno...

Tungsten trioxide microspheres of 2–4 m diameter have been prepared by controlled oxidation of tungsten carbide microspheres. These microspheres are characterized by XRD, SEM, and HRTEM. The microspheres are made of WO3 nanoparticles with an average diameter of around 15 nm. Platinum supported on these WO3 microspheres exhibits higher and stable electrocatalytic activity for methanol oxidation ...

Thin films of tungsten trioxide were deposited on quartz substrates by RF magnetron sputtering. Different annealing temperatures in the range from 423 to 973 K were used under ambient atmosphere. The influence of the annealing temperature on the structure and optical properties of the resulting WO3 thin films were studied. The surface morphology of the films is composed of grains with an averag...

Printed electrochromic flexible films were obtained by combining transparent silver grid electrodes formed by self-assembly and inkjet printed WO3 nanoparticles. Concentrated dispersions of WO3 nanoparticles were inkjet printed on transparent plastic silver grid electrodes with a high transparency of 83% in the spectral range of 400-800 nm, and a low sheet resistance in the range of 1-5 Ω sq(-1...

A series of model-supported WO3 catalysts were synthesized on preformed Al2O3, Nb2O5, TiO2, and ZrO2 supports by impregnation of aqueous ammonium metatungstate, (NH4)10W12O41·5H2O. The molecular and electronic structures of the supported tungsten oxide phases were determined with in situ Raman and UV–vis spectroscopy, respectively. The supported tungsten oxide structures are the same on all oxi...