Novel low-dimensional thermoelectric (TE) materials suffer from poor mechanical reliability, which limits their applications, especially in mechanically harsh environments. Here, we propose a new concept, in which the novel, abundant, thermally stable TE-nanostructures are dispersed and then intimately embedded inside a protective, mechanically reliable tetragonal ZrO2 (TZP) ceramic matrix with...

We studied the adrenosuppressive effect of antiandrogen TZP-4238 and its metabolites. The binding affinity for the corticosteroid receptor using rat hepatic cytosol was in the order 11-OH TZP-4238 > 11, 15-(OH)2 TZP-4238 >> TZP-4238 > or = 15-OH TZP-4238 > 11-keto TZP-4238. Male beagle dogs aged 1-6 years were randomly divided into TZP-4238 (0.05, 0.5mg/kg) treatment groups and CMA (0.5mg/kg) t...

ceramic dental materials have been considered as alternatives to metals for dental implants application. in this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. because of its good mechanical properties and color similar to tooth. the aim and novelty of this study was to design and prepare y-t...

Objective: To evaluate the hydrothermal aging effect on the translucency of partially stabilized tetragonal zirconia with yttria (Y-TZP) used as monolithic or fully milled zirconia and of core type. Methods: Twenty disc-shaped specimens (1 and 10 mm) for each type of monolithic and core Y-TZP materials were milled and sintered according to the manufacturer's instruction. The final specimens wer...

The aim of this study was to determine the machinability of new silica-doped Y-TZP by CAD/CAM and the resistance to low temperature degradation of the milled sample by comparing with a commercial HIP type Y-TZP material. The copings could be milled from silica-doped Y-TZP blocks without chipping, and there was no significant difference between the two types of Y-TZP materials in either the marg...

The objective of this study was to establish the mechanism(s) controlling degradation of yttria-tetragonally-stabilized zirconia (Y-TZP) powder in aqueous suspensions and determine the significance of this degradation to the aqueous physical chemistry of Y-TZP. Experiments were performed on commercially available Y-TZP powder placed in aqueous suspensions at 25°C. Experimental investigations in...

This study investigated the influence of surface roughness and cyclic loading on fatigue resistance in Y-TZP subjected to hot isostatic pressing (HIP). Fifty Y-TZP cylinders 3.0 mm in diameter were divided into Group A (polished by centerless method; TZP-CP) or Group B (blasted and acid-etched: TZP-SB150E). Twenty five cp-titanium cylinders (Ti-SB150E) were used as a control. Static and cyclic ...

It was indicated that tetragonal zirconia polycrystal (TZP) containing yttria (Y₂O₃) and niobium oxide (Nb₂O₅) ((Y,Nb)-TZP) could be an adequate dental material to be used at esthetically important sites. The (Y,Nb)-TZP was also proved to possess its osteogenic potential comparable with those conventional dental implant material, titanium (Ti). The objective of the current study was to characte...

The aim of this investigation was to determine the influence of simulated ageing on the tetragonal-to-monoclinic phase transformation and on the flexural strength of a 3Y-TZP ceramic, compared to alumina toughened zirconia (ATZ) and ceria-stabilized zirconia (12Ce-TZP). Standardized disc specimens of each material were hydrothermally aged in steam at 134°C and 3bar for 0, 16, 32, 64 or 128h. Th...

The aim of this in vitro study was to investigate the wear behavior of the abrader when tetragonal zirconia polycrystal (TZP), cp-titanium (CpTi) and Ti-6Al-4V alloy (TiAlV) were used as the antagonist on fixed dental prostheses (FDPs). Both hemisphere abrader and flat substrate specimens were prepared using TZP, CpTi and TiAlV. Two-body wear tests were performed in distilled water, and the wea...