objective: the purpose of this study was to evaluate the transverse strength of one brand of denture base material repaired with two autopolymerized acrylic resins with and without wire reinforcement. materials and methods: eighty samples (2.5×10×65 mm3) were fabricated and divided into five groups. the control group was left intact. groups b and d specimens were repaired with autopolymerizing ...

statement of problem: fracture strength of a denture base resin is of great concern, and many approaches have been used to strengthen acrylic resin dentures. purpose: the aim of this study was to measure the transverse strength of a heat polymerized acrylic resin, after reinforcement with metal wire and two types of glass fibers. materials and methods: forty rectangular specimens (65.0×10.0×3.3...

background : denture fracture is an unresolved problem in complete denture prosthodontics. however, the repaired denture often experiences a refracture at the repaired site due to poor transverse strength. hence, this study was conducted to evaluate the effect of joint surface contoursand glass fiber reinforcement on the transverse strength of repaired acrylic resins. materials and methods: a t...

objective: reinforcement with fiber is an effective method for considerable improvement in flexural properties of indirect composite resin restorations. the aim of this in-vitro study was to compare the transverse strength of composite resin bars reinforced with preimpregnated and non-impregnated fibers. materials and methods: thirty six bar type composite resin specimens (3×2×25 mm) were const...

objective: the aim of this study was to measure and compare the transverse strength and deflection of two acrylic resins. method and materials: a total of 30 samples, with dimensions of 2.5×10×65mm, were prepared with acropars and meliodent acrylic resins according to ada specification no. 12. the specimens were divided into two groups of 15 samples each. a three-point bending test was carried ...

The influence of specimen polishing, specimen configuration, and specimen size on the transverse tension strength of two glass epoxy materials loaded in three and four point bending was evaluated. Polishing machined edges, and/or tension side failure surfaces, was detrimental to specimen strength characterization instead of yielding a higher, more accurate, strength as a result of removing inhe...

INTRODUCTION As civilization has progressed, there has been continued refinement of materials available for dental practice. The applications of resins have been extended to increased practical uses in numerous areas of prosthetic and restorative dentistry. Certain significant alterations in the technique of manipulation and nature of the dental product have influenced the range of application ...