Abstract:Nanostructured titania was synthesized by colloidal and polymeric sol-gel routes. Stable colloidal and polymeric titania sols were prepared by adjusting the proper values of the acid/alkoxide and the water/alkoxide molar ratios. The properties of sols were determined by dynamic light scattering technique and synthesized titania was characterized by thermogravimetry and differential the...

Textural evolution (porosity reduction, pore and crystallite growth) in titania-alumina composite membranes has been studied using thermal analysis, X-ray diffraction, field emission scanning electron microscopy and N, physisorption techniques. The presence of alumina in the membranes improved the thermal stability of the porous texture by retarding the anatase-to-rutile phase transformation a...

Silica-titania monoliths with micrometer-scale macroporous and nanometer-scale mesoporous structure and high titania contents are prepared by sol-gel process and phase separation. Titanium alkoxide precursor was not effective in the preparation of high titania content composites because of strong decrease in phase separation tendency. Bimodal porous gels with high titania content were obtained ...

The main objective of this work was to prepare nanosized titania (TiO2) particles by mixed reverse microemulsion route. In this work titania was prepared by quaternary microemulsion system (water/surfactant/co-surfactant/ oil-phase). Span-80, Aerosol-OT, n-Propanol, Isooctane, and Titanium tetra isopropoxide (TTIP) were used as surfactant, co-surfactant, oil-phase and titania precursor respecti...

Titania microspheres were synthesized using hydrothermal methods to exploit a new liquid chromatography stationary phase. The prepared titania microspheres were approximately 7 μm in diameter, and the particle size distribution was relatively narrow and uniform. Furthermore, the average specific surface area was 276.0 m2·g−1, the average pore volume was approximately 0.25 mL·g−1, and the pore d...

the photocatalytic coatings were prepared via incorporating the modified titania nanoparticles into epoxy-based inorganic-organic hybrid coatings. titania nanoparticles were first synthesized from tetra-n-butyl titanate using sol-gel methods by two different calcination treatments, i.e., in mild condition (80°c) and 500°c. the formed anatase nanoparticles were further modified as titania-silica...

The photocatalytic coatings were prepared via incorporating the modified titania nanoparticles into epoxy-based inorganic-organic hybrid coatings. Titania nanoparticles were first synthesized from tetra-n-butyl titanate using sol-gel methods by two different calcination treatments, i.e., in mild condition (80°C) and 500°C. The formed anatase nanoparticles were further modified as Titania-Silica...

The photocatalytic coatings were prepared via incorporating the modified titania nanoparticles into epoxy-based inorganic-organic hybrid coatings. Titania nanoparticles were first synthesized from tetra-n-butyl titanate using sol-gel methods by two different calcination treatments, i.e., in mild condition (80°C) and 500°C. The formed anatase nanoparticles were further modified as Titania-Silica...