We report a simple biogenic-route to narrow the band gap of TiO2 nanocrystals for visible light application by offering a greener method. When an electrochemically active biofilm (EAB) was challenged with a solution of Degussa-TiO2 using sodium acetate as the electron donor, greyish blue-colored TiO2 nanocrystals were obtained. A band gap study showed that the band gap of the modified TiO2 nano...

Nitrogen/sulfur co-doped anatase TiO2 nanocrystals with a high specific surface area and a high percentage of {001} facets were synthesized by a solvent-thermal process followed by the calcination with thiourea at an optimum heat treatment temperature. Under current experimental conditions, the optimum heat treatment temperature was found at 300°C, which successfully introduced nitrogen and sul...

titanium dioxide nanocrystals were synthesized by sol-gel method at room temperature. titanium isoprophoxide and absolute ethanol were used as precursors to prepare the sol. the ph of the solution was adjusted by adding nitric acid and sodium hydroxide solution. the prepared tio2 nanocrystals were annealed at 325°c, 425°c and 525°c respectively. the effect of ph on the surface morphology and st...

A facile hydrothermal approach has been developed to prepare defective TiO2-x nanocrystals using Ti(III)-salt as a precursor and L-ascorbic acid as reductant and structure direction agent. The prepared TiO2-x nanocrystals are composed of a highly crystallized TiO2 core and a disordered TiO2-x outer layer, possessing high surface area, controlled oxygen vacancy concentration and tunable bandgap ...

Titanium dioxide nanocrystals were synthesized by sol-gel method at room temperature. Titanium isoprophoxide and absolute ethanol were used as precursors to prepare the sol. The pH of the solution was adjusted by adding nitric acid and sodium hydroxide solution. The prepared TiO2 nanocrystals were annealed at 325°C, 425°C and 525°C respectively. The effect of pH on the surface morphology and st...

We report a non-trivial facile chemical approach using ionic liquid ([bmim][Cl]) as a porogen for the synthesis of (001) faceted TiO2 nanocrystals having mesoscopic void space. This faceted TiO2 nanomaterial has been doped with Pt nanoclusters through chemical impregnation. The resulting Pt-doped TiO2 nanomaterials are thoroughly characterized by powder X-ray diffraction (PXRD), Raman spectrosc...

Anatase TiO2 nanocrystals doped with nitrogen and sulfur, where substitutional N and S atoms for lattice O, respectively, locate in the bulk and the surface layer of the crystals, were designed and prepared. As a result of remarkably lowered electronic resistance, the N/S doped TiO2 shows a superior high rate lithium storage capability to that of reference TiO2 nanocrystals, though the former h...

Few-layer graphene/TiO2 nanocrystal composites are successfully in situ synthesized at a low temperature of 400 °C using C28H16Br2 as the precursor. Raman mapping images show that the TiO2 nanocrystals are very uniformly dispersed in the composite films, and the in situ coating during the thermal decomposition process will favor the formation of a good interface combination between the few-laye...

While the synthesis of TiO2 hollow structures is well-established, in most cases it is particularly difficult to control the crystallization of TiO2 in solution or by calcination. As a result, TiO2 hollow structures do not really exhibit enhanced lithium storage properties. Herein, we report a simple and cost-effective template-assisted method to synthesize anatase TiO2 hollow spheres composed ...

To photo-catalytically degrade RhB dye using solar irradiation, CeO2 doped TiO2 nanocomposites were synthesized hydrothermally at 700 °C for 9 hrs. All emission spectra showed a prominent band centered at 442 nm that was attributed to oxygen related defects in the CeO2-TiO2 nanocrystals. Two sharp absorption bands at 1418 cm-1 and 3323 cm-1 were attributed to the deformation and stretching vibr...