In turbine engines, high temperature components made of superalloys may crack in a creep process during service. With the inward flux of the gases, e.g. oxygen and nitrogen, along those cracks, the microstructure of the superalloy substrate nearby the cracks may degrade by internal oxidation and nitridation. The aim of this study is to investigate and simulate the oxidation-nitridation-induced ...

The fatigue behavior of a nickel-base superalloy was investigated under total strain-controlled mode at high temperature. The fatigue life, cyclic stress response behavior and hysteresis loop of the superalloy were investigated under isothermal low cycle fatigue (LCF) conditions. The superalloy exhibited cyclic hardening and softening behaviors during the process of fatigue loading. The hystere...

A variety of cast pyrometR 718 alloy microstructures result from processing of different diameters of industrial scale ingots for producing superalloy forgings used in aircraft turbine engine applications. The hot workability of these cast alloys will significantly depend on the cast microstructure. The current study is focussed on understanding the evolution of the cast microstructure during V...

The dimensionless Niyama criterion was used to predict the formation of microporosity in nickel-based superalloy casting, which extended the model application from a simple plate casting to complex thin-wall superalloy casting. The physical characteristics of the superalloy were calculated by JMatPro software. The relation between the volume percentage of microporosity and the dimensionless Niy...

A new method to adjust the pore size in superalloy membranes is shown, utilizing controlled cooling from solution heat treatment of the solid superalloy. Hereby, the nucleation rate and, thus, the size of the γ'-precipitates can be varied to a large extent. This leads to a corresponding variation in the pore size once the membrane material is produced by directional coarsening of the γ'-phase t...

We experimentally investigate the influence of an alternating electromagnetic field on the surface and internal qualities of Incoloy800H superalloy billets. The electromagnetic continuous casting experiments for Incoloy800H superalloy were successfully conducted and the billets (0.1 m ˆ 0.1 m ˆ 1.2 m) were obtained. We figure out that the high frequency (20.4 kHz) electromagnetic field which is...

A Rayleigh number based criterion is developed for predicting the formation of freckles in Ni-base superalloy castings. This criterion relies on finding the maximum local Rayleigh number in the mush, where the ratio of the driving buoyancy force to the retarding frictional force is the largest. A critical Rayleigh number for freckle formation of approximately 0.25 is found from available experi...

Purpose. To evaluate stent lumen visibility of a large sample of different peripheral arterial (iliac, renal, carotid) stents using magnetic resonance angiography in vitro. Materials and Methods. 21 different stents and one stentgraft (10 nitinol, 7 316L, 2 tantalum, 1 cobalt superalloy, 1 PET + cobalt superalloy, and 1 platinum alloy) were examined in a vessel phantom (vessel diameters ranging...

Investigations on femtosecond laser micromachining of single crystal superalloys with and without plasma-sprayed thermal barrier coatings were conducted under laser fluences ranging from 0.1 J/cm up to 160 J/cm. Micromachining was carried out in air using a titanium:sapphire laser system ( = 780 nm) operating at a repetition rate of 1 kHz and delivering individual pulses of ~150 fs duration. Th...

hydromechanical deep drawing (hdd) is one of the most convenient processes in which a sheet metal is drawn against a counter pressure rather than a rigid die in conventional stampings. this process has been increasingly used to produce aerospace and automotive components. more recently, aerospace industry is demanding new materials with capability to produce high strength to weight ratio produc...