The corrosion fatigue performance of high-strength bolt was studied. Based on the fracture mechanics theory and the Gerberich-Chen formula, the high-strength bolt corrosion fracture crack model and the fatigue life model were established. The high-strength bolt crack depth and the fatigue life under corrosion environment were quantitatively analyzed. The factors affecting high-strength bolt cor...

A series of stress corrosion experiments were performed on 12 pultruded glass fiber composite materials (two fibers in six different matrices) commonly used in high voltage composite insulators. In this study two types of glass fibers were investigated, namely Eglass and ECR-glass. The tests were performed in nitric acid solutions (pH 1.2) using constant K I specimens that were specifically des...

The various mechanisms that have been put forward to explain stress-corrosion cracking are briefly summarized. The experimental observations of stress-corrosion cracking in titanium alloys in widely different environmer a are discussed. Evidence from the literature for and against the possibility that hydrogen plays a role in the stress-corrosion cracking of titanium alloys is documented. An ex...

The purpose of this work is to establish the critical surface conditions leading to the initiation of stress corrosion cracks on the as supplied surfaces of three unidirectional Eglass/polymer composites with modified polyester, epoxy and vinyl ester resins subjected to a nitric acid solution without mechanical loads. The composite materials considered in this study are commonly used in composi...

Unusually rapid closure of stressed fractures, observed in the initial stages of loading and at low temperatures, is examined using models for subcritical crack growth and pressure solution. The model for stress corrosion examines tensile stress concentrations induced at the Hertzian contact of propping fracture asperities, and mediates fracture growth according to a kinetic rate law. Conversel...

Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...

The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens eithe...

ion of Models of Stress Corrosion Cracking of Drip Shield and Waste Package Outer Barrier and Hydrogen Induced Corrosion of Drip Shield TABLE OF CONTENTS Page 1. PU R P O SE ............................................................................................................................... 8 2. QUALITY ASSURANCE .............................................. 8 3. COMPUTER SOFTWARE AN...

Finite element analyses were conducted to clarify the role of corrosion product films (CPFs) in stress corrosion cracking (SCC). Flat and U-shaped edge-notched specimens were investigated in terms of the CPF-induced stress in the metallic substrate and the stress in the CPF. For a U-shaped edge-notched specimen, the stress field in front of the notch tip is affected by the Young's modulus of th...