a hydrothermal method for preparation of nano-size zirconia has been studied to optimize the effective parameters (precursor concentration, temperature and time) using response surface methodology (rsm). the synthesized zirconia samples were characterized through x-ray diffraction (xrd), scanning electron microscope (sem) and transmission electron microscopy (tem) analyses to identify mean nano...

nanocomposite of zro2/zno was prepared under ultrasonic irradiation by sol gel process from directly mixing zirconium and zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°c for 3h in furnace. the precursor sol of zirconium was prepared from an aqueous solution of zrcl4 and zinc acetate dihydrated was...

The phases of ceria–zirconia nanoparticles observed in air are studied as a function of particle size and composition by X-ray diffraction, transmission electron microscopy, and Raman spectroscopy. The emergence of two tetragonal phases t00 and t monotonically moves toward higher zirconia concentrations with decreasing particle size. A smaller particle size increases the solubility of zirconia ...

Nanosized sulfated zirconia with Brønsted acidic sites has been prepared by a simple calcination in the absence of any solvent. XRD patterns reveal that the sulfated zirconia mainly consists of tetragonal crystalline zirconia with average size of about 7 nm, which is further confirmed by TEM images. N2 adsorption data show that the nanosized sulfated zirconia has high surface area (165-193 m2/g...

Zirconia ceramics with porous structure have been prepared by solid-state reaction using yttria-stabilized zirconia and stearic acid powders. Analysis of its microstructure and phase composition revealed that a pure zirconia phase can be obtained. Our results indicated that its porosity and pore size as well as the mechanical characteristics can be tuned by changing the content of stearic acid ...

A hydrothermal method for preparation of nano-size zirconia has been studied to optimize the effective parameters (precursor concentration, temperature and time) using response surface methodology (RSM). The synthesized zirconia samples were characterized through X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscopy (TEM) analyses to identify mean nano...

PURPOSE The opacity of zirconia is an esthetic disadvantage that hinders achieving natural and shade-matched restorations. The aim of this study was to evaluate the translucency of non-colored and colored framework zirconia and monolithic zirconia. MATERIALS AND METHODS The three groups tested were: non-colored framework zirconia, colored framework zirconia with the A3 shade according to Vita...

This study investigated the contrast ratio and grain size depending on sintering parameters of twelve different zirconia materials and compared with glass-ceramic (N=156, n=12 per group). Contrast ratio of all ceramics was measured using a spectrophotometer according to ISO 2471: 2008. Grain sizes of zirconia were determined by SEM. Data was analyzed using one-way ANOVA followed by post-hoc Sch...

PURPOSE This study aimed to identify the effects of the sintering conditions of dental zirconia on the grain size and translucency. MATERIALS AND METHODS Ten specimens of each of two commercial brands of zirconia (Lava and KaVo) were made and sintered under five different conditions. Microwave sintering (MS) and conventional sintering (CS) methods were used to fabricate zirconia specimens. Th...

PURPOSE To measure the surface loss of dental restorative zirconia and the short-term bond strength between an indirect composite resin (ICR) and zirconia ceramic after various sandblasting processes. MATERIALS AND METHODS Three hundred zirconia bars were randomly divided into 25 groups according to the type of sandblasting performed with pressures of 0.1, 0.2, 0.4 and 0.6 MPa, sandblasting t...