in the present work, the influence of aging temperature on mechanical properties and sound velocity of maraging steel m350 was investigated. for this purpose, first, samples were solution annealed at 825◦c for 2 hours and then age hardened at 510◦c-600◦c for 3 hours. hardness, tensile and impact tests were used for determining mechanical properties and longitudinal ultrasonic velocity was used ...

Nano/submicron austenitic stainless steels have attracted increasing attention over the past few years due to fine structural control for tailoring engineering properties. At the nano/submicron grain scales, grain boundary strengthening can be significant, while ductility remains attractive. To achieve a nano/ submicron grain size, metastable austenitic stainless steels are heavily cold-worked,...

Data about an effect of cyclic γ-α-γ martensitic transformations on the structure state of reverted austenite Fe-31.7 wt.% Ni-0.06 wt.% C alloy are presented. The effect of multiple direct γ-α and reverse α-γ martensitic transformations on fragmentation of austenitic grains has been investigated by electron microscopy and X-ray diffraction methods. An ultrafine structure has been formed by nano...

Diffusion characteristics of iron and nickel atoms were investigated using radioactive isotopes method in phase-hardened metastable iron-nickel Fe-31.7%Ni-0.06%C alloy with nanofragmented structure. It has been found that diffusion mobility of nickel and iron atoms in reverted austenite of Fe-31.7%Ni-0.06%C alloy significantly increases as the result of multiple γ-α-γ martensitic transformation...

In this paper, an advanced thermo-mechanical treatment was conducted on AISI 316 austenitic stainless steel. At first, three samples were rolled at the ambient temperature, the temperature of -20 ºC (dry ice and ethanol) and -196 ºC (liquid nitrogen). Then, the samples were annealed at 800 ºC in the time range of 1 to 15 minutes. In each step, the microhardness values of the samples were measur...

In the present work, the influence of aging temperature on mechanical properties and sound velocity of Maraging steel M350 was investigated. For this purpose, first, samples were solution annealed at 825◦C for 2 hours and then age hardened at 510◦C-600◦C for 3 hours. Hardness, tensile and impact tests were used for determining mechanical properties and longitudinal ultrasonic velocity was used ...