In the present paper, a study of the effects of fabric weight, fiber cross-sectional shapes (round, hollow and trilobal) and presence of reinforcing material on the compression properties (initial thickness, percentage compression, percentage thickness loss and percentage compression resilience) of polyester needle punched industrial nonwoven fabrics is presented. It was found that for fabrics ...

here, in situ synthesis of nano zinc oxide, along with aminolysis of polyester fabric, has simultaneously been carried out by using triethanol amine (tea) and zinc acetate. the zno nano particles (nps) were formed and stabilized on the fabric surface by amine compound at 130 °c for 1 h. the synthesis of nano zno particles on the polyester fabric were confirmed by x-ray diffraction (xrd) pattern...

The presence of defects in cold mercerizing of cotton goods led to the creation of a new method, called hot mercerizing in which caustic soda solution is used at a high temperature. Hot mercerizing is successfully used in cotton blended with some other fibers. In cotton/polyester blend fabrics, this treatment serves a dual purpose: subjectively, it imparts a silklike soft handle to the po...

The presence of defects in cold mercerizing of cotton goods led to the creation of a new method, called hot mercerizing in which caustic soda solution is used at a high temperature. Hot mercerizing is successfully used in cotton blended with some other fibers. In cotton/polyester blend fabrics, this treatment serves a dual purpose: subjectively, it imparts a silklike &#10&#10&#10soft handle to ...

Here, in situ synthesis of nano zinc oxide, along with aminolysis of polyester fabric, has simultaneously been carried out by using triethanol amine (TEA) and zinc acetate. The ZnO nano particles (NPs) were formed and stabilized on the fabric surface by amine compound at 130 °C for 1 h. The synthesis of nano ZnO particles on the polyester fabric were confirmed by X-ray diffraction (XRD) pattern...

Here, in situ synthesis of nano zinc oxide, along with aminolysis of polyester fabric, has simultaneously been carried out by using triethanol amine (TEA) and zinc acetate. The ZnO nano particles (NPs) were formed and stabilized on the fabric surface by amine compound at 130 °C for 1 h. The synthesis of nano ZnO particles on the polyester fabric were confirmed by X-ray diffraction (XRD) pattern...

Nano-ZnO was prepared by direct precipitation method with zinc chloride and sodium carbonate anhydrous as raw materials, and its particle size and dispersion were characterized by TEM. The effects of concentration and the ratio of reactants and reaction temperature on its dispersion in aqueous solution were analyzed and the best reaction conditions were as follows: reaction temperature 60 , ult...

The disinfection of surfaces in the immediate surrounding of a hospitalised patient is considered to be an important element for prevention of nosocomial infection. The type of fabric in a mop, however, has to our knowledge never been regarded as relevant for an effective disinfection of surfaces. We have therefore studied the adsorption of benzalkonium chloride (BAC), glutardialdehyde and prop...

The present paper reports a detailed study on heat and moisture vapour transmission characteristics of different types of multilayered fabric ensembles. Two sets of multilayered fabrics have been prepared. In first set, two types of carded web produced from acrylic and polyester fibres with five different areal densities in each fibre type have been used as middle layer. In second set, differen...

cotton/polyester knitted fabrics as a major production of textile industry was treated with titanium dioxide nanosized particles. the treated fabric with nanosized tio2 became whiter with a good self-cleaning property. also the discoloration of reactive black 5 dye was studied and reported. the stabilization of tio2 on cotton/polyester knitted fabrics by citric acid (ca) with sodium hypophospha...