We report the electrochemical performance of porous NASICON-type Li3Fe2(PO4)3 thin films to be used as a cathode for Li-ion microbatteries. Crystalline porous NASICON-type Li3Fe2(PO4)3 layers were obtained by radio frequency sputtering with an annealing treatment. The thin films were characterized by XRD, SEM, and electrochemical techniques. The chronoamperometry experiments showed that a disch...

The molecular basis for Na/Li exchange is unknown. Li can be transported by the Na pump, anion exchanger (AE1), a background leak, and the Na/Li exchanger. In vivo the intraerythrocyte concentration of Li results from the balance of passive entry, mostly on AE1, and the active extrusion on the Na/Li exchanger. Here we show that erythrocytes have Li-activated PO4 transport that behaves as if it ...

The human response to acute phosphate (PO4) loading is poorly characterized, and it is unknown whether an intestinal phosphate sensor mechanism exists. Here, we characterized the human mineral and endocrine response to parenteral and duodenal acute phosphate loads. Healthy human participants underwent 36 hours of intravenous (IV; 1.15 [low dose] and 2.30 [high dose] mmol of PO4/kg per 24 hours)...

In order to better understand the influence and mechanism of soil-derived humic acid (SHA) on adsorption of P onto particles in soils, the amounts of PO4 adsorbed by synthetic goethite (a-FeOOH) were determined at different concentrations of SHA, pH, ionic strength and order of addition of adsorbents. Addition of SHA can significantly reduce the amount of PO4 adsorption as much as 27.8%. Both g...

Since in situ formation of Mg(OH)2 can efficiently sorb phosphate (PO4) from low concentrations in the environment, a novel dispersed magnesium oxide nanoflake-modified diatomite adsorbent (MOD) was developed for use in restoration of eutrophic lakes by removal of excess PO4. Various adsorption conditions, such as pH, temperature and contact time were investigated. Overall, sorption capacities ...

Mango stone biocomposite efficiency for the removal of phosphate ions (PO4) from aqueous solution was investigated as a function of pH (2–8), biocomposite dose (0.05–0.40 g/100 mL solution), contact time (5–120 min), initial PO4 ions concentration (20–800 mg/L) and temperature (33–61 C). Maximum PO4 ions removal was achieved at pH 2, biocomposite dose 0.3 g, contact time 90 min and initial PO4 ...

Measurement of polymerization degree of condensed phosphates was examined by solid-state NMR. Broad peaks of the NMR of endand middle-PO4 groups of condensed phosphates were observed at about 1 and -20 ppm, respectively. The NMR. peak area ratio (Ro) of middle-PO4 group to end-PO4 group has the following relation with the polymerization degree (n) of polyphosphate: Ro (middle-PO4/end-PO4) = (n-...

Sodium-ion batteries, representative members of the post-lithium-battery club, are very attractive and promising for large-scale energy storage applications. The increasing technological improvements in sodium-ion batteries (Na-ion batteries) are being driven by the demand for Na-based electrode materials that are resource-abundant, cost-effective, and long lasting. Polyanion-type compounds are...

Synechococcus sp. WH 8102 is a motile marine cyanobacterium isolated originally from the Sargasso Sea. To test the response of this organism to cadmium (Cd), generally considered a toxin, cultures were grown in a matrix of high and low zinc (Zn) and phosphate (PO4 (3-)) and were then exposed to an addition of 4.4 pM free Cd(2+) at mid-log phase and harvested after 24 h. Whereas Zn and PO4 (3-) ...

OBJECTIVE To investigate the feasibility of nitrogen and phosphorus recovery from swine waste biogas digester effluent and the effects of pH and NH4+: Mg2+: PO4(3-) molar ratio on its precipitation. METHODS Precipitation experiments with swine waste biogas digester effluent were conducted at pH 7.5, 8.0, 8.5, and 9.0 together with NH4+: Mg2+: PO4(3-) molar ratios 1: 0.2: 0.08, 1: 1: 1, and 1:...