a palladium composite membrane was prepared via electroless plating technique using organic-inorganic method during activation process. the ceramic support surface was modified by two tio2-boehmite and one γ-alumina layers to avoid pd penetration in support pores. thin and defect-free pd composite membrane was obtained by creating a relative smoothness on the ceramic support and using pd nanopa...

due to unique applications of palladium nanoparticles, synthesis of these nanoparticles by a simple andlow cost method is very important. in this work, pd nanoparticles were synthesized with narrow sizedistribution by loading metal salt (pd(oac)2 ) into the polymeric matrix (peg) as reducing agent andstabilizer. also, the effect of metal salt concentration and peg molecular weight on the conver...

Due to unique applications of palladium nanoparticles, synthesis of these nanoparticles by a simple and low cost method is very important. In this work, Pd nanoparticles were synthesized with narrow size distribution by loading metal salt (Pd(OAc)2 ) into the polymeric matrix (PEG) as reducing agent and stabilizer. Also, the effect of metal salt concentration and PEG molecular weight on the con...

In this research work, copper (Cu), palladium (Pd) and their bimetallic palladium@ copper (Pd@Cu) nanoparticles were synthesized using trisodium citrate as a stabilizing agent using the known chemical reduction method. The synthesized Cu, Pd and Pd@Cu nanoparticles were characterized by the ultraviolet-visible spectroscopy, scanning electron microscopy and X-ray diffraction spectroscopy, respec...

Core-shell nanoparticles often exhibit improved catalytic properties due to the lattice strain created in these core-shell particles. Herein, we demonstrate the synthesis of core-shell Au@Pd nanoparticles from their core-shell Au@Ag/Pd parents. This strategy begins with the preparation of core-shell Au@Ag nanoparticles in an organic solvent. Then, the pure Ag shells are converted into the shell...

Monodisperse bimetallic Pd-Cu nanoparticles with controllable size and composition were synthesized by a one-step multiphase ethylene glycol (EG) method. Adjusting the stoichiometric ratio of the Pd and Cu precursors afforded nanoparticles with different compositions, such as Pd(85)-Cu(15), Pd(56)-Cu(44), and Pd(39)-Cu(61). The nanoparticles were separated from the solution mixture by extractio...

Palladium nanoparticles of average size around 8 nm have been synthesized rapidly by UV irradiation of mixture of palladium chloride and potassium oxalate solutions. A rod-shaped palladium oxalate complex has been observed as an intermediate. In the absence of potassium oxalate, no Pd nanoparticles have been observed. The synthesized Pd nanoparticles have been characterized by powder X-ray diff...

Palladium (Pd) nanoparticles were deposited on the surface of halloysite nanotubes (HNTs) modified with γ-aminopropyltriethoxysilane (APTES) to produce Pd/NH2-HNTs nanocomposites. The results indicated that Pd nanoparticles were densely immobilized onto NH2-HNTs with an average diameter of ~ 3 nm. The Pd distribution on the surface of silanized HNTs showed much more uniform, and the Pd nanopart...

The aging of both Pt−Pd nanoparticles and core− shell Pt−Pd nanoparticles has been reported to result in alloying of Pt with Pd. In comparison to monometallic Pt catalysts, the growth of Pd−Pt bimetallics is slower; however, the mechanism of growth of particles and the mechanism by which Pd improves the hydrothermal durability of bimetallic Pd−Pt particles remains uncertain. In our work on hydr...

A green synthesis of gold and silver nanoparticles is described in the present report using platycodon saponins from Platycodi Radix (Platycodon grandiflorum) as reducing agents. Platycodin D (PD), a major triterpenoidal platycodon saponin, was enriched by an enzymatic transformation of an aqueous extract of Platycodi Radix. This PD-enriched fraction was utilized for processing reduction reacti...