steel 2205 is one of the most famous duplex stainless steels. the microstructure of this steel composed of ferrite and austenite in similar amount. therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. it is not possible to employ the usual heat treatment. it shows the importance of ...

Steel 2205 is one of the most famous duplex stainless steels. The microstructure of this steel composed of ferrite and austenite in similar amount. Therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. It is not possible to employ the usual heat treatment. It shows the importance of ...

the flow stress of steel depends significantly on microstructural changes taken place during hot deformation processes. in hot deformation processes, the flow stress of steel is influenced by two main metallurgical phenomena, i.e. recovery and recrystallization, along with its chemical composition and thermo-mechanical parameters. the final mechanical properties of steel are also determined by ...

The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...

In hot forming process, the workpiece undergoes plastic deformation at high temperature and the microstructure of the workpiece changes according to the plastic deformation. These changes affect the mechanical properties of workpiece. In order to optimize this process, both the plastic deformation of workpiece and its microstructural changes should be taken into consideration. Since material be...

In hot forming process, the workpiece undergoes plastic deformation at high temperature and the microstructure of the workpiece changes according to the plastic deformation. These changes affect the mechanical properties of workpiece. In order to optimize this process, both the plastic deformation of workpiece and its microstructural changes should be taken into consideration. Since material be...

The high one-pass deformation behaviors of mass-produced Al–4.30Mg alloy are investigated in the temperature ranging 350 °C–500 °C, strain rate 0.01 s?1–1 s?1 and reduction 50–75%. 3D processing maps constructed by superimposition instability map power dissipation at true 0.69, 0.92, 1.20 1.38. When increases from 0.69 to 1.38, average apparent activation energy (Q) decreases 140.3 kJ/mol 112.7...

strain induced precipitation in hsla-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°c to 1100°c and strain rate of 0.001s-1 to 1s-1. the absence of dynamic recrystallization at temperatures below 1000°c was attributedto the influence of dynamic precipitation. the stress relaxation tests showed that strain inducedprecipitation is possible...