Nanotechnology is an area of intense commercial development, and concerns have been raised about the possible impacts to the environment. Zinc oxide nanoparticles (nanoZnO) are used in transparent sunscreens and may find their way into the environment through wastewater treatment plants and through skin contact with water. The purpose of this study was to examine the bioavailability of Zn in fa...

Nano hexagonal wurtzite ZnO has been prepared on zeoliteA by the sono-chemical method. The zeoliteA was mixed into Zinc gel, after stirring for two days, the mixture was irradiated 30 min by ultrasonic probe. The filtrated composite gel was calcinated at 500°C for 3h in furnace. The produced composite was characterized using X-ray diffraction, FT-IR spectroscopy and field emission scanning elec...

Nano hexagonal wurtzite ZnO has been prepared on zeoliteA by the sono-chemical method. The zeoliteA was mixed into Zinc gel, after stirring for two days, the mixture was irradiated 30 min by ultrasonic probe. The filtrated composite gel was calcinated at 500°C for 3h in furnace. The produced composite was characterized using X-ray diffraction, FT-IR spectroscopy and field emission scanning elec...

easily prepared nanozno was found to be as an efficient catalyst in the synthesis of 1,4-dhps via four-component reaction of 1,3-dicarbonyls, aldehydes and ammonium carbonate in water at 60 °c. the prepared nanozno was characterized by xrd and ft-ir analysis, while the determined specific surface area of nano catalyst by bet method was 33 m2/g.

Easily prepared nanoZnO was found to be as an efficient catalyst in the synthesis of 1,4-DHPs via four-component reaction of 1,3-dicarbonyls, aldehydes and ammonium carbonate in water at 60 °C. The prepared nanoZnO was characterized by XRD and FT-IR analysis, while the determined specific surface area of nano catalyst by BET method was 33 m2/g.

Easily prepared nanoZnO was found to be as an efficient catalyst in the synthesis of 1,4-DHPs via four-component reaction of 1,3-dicarbonyls, aldehydes and ammonium carbonate in water at 60 °C. The prepared nanoZnO was characterized by XRD and FT-IR analysis, while the determined specific surface area of nano catalyst by BET method was 33 m2/g.

In the current study, electrochemical removal of reactive orange 7 (RO7) dye in aqueous solution was examined over a novel Ti/nanoZnO–CuO electrode prepared through electrophoretic deposition technique. Surface morphology, crystal structure, and elemental investigation were done by Field emission scanning electron microscopy, X-ray energy dispersive spectrometry, diffraction analysis, which con...

BACKGROUND This study aimed to evaluate the effects of several mouthwashes containing nanoparticles on discoloration of dental enamel, and compare the results with that of 0.2% chlorhexidine (CHX). MATERIAL AND METHODS Sixty intact premolars were randomly assigned to six groups. A spectrophotometer was used to measure the color of the teeth (T1) according to the CIELAB system. The specimens i...

The objective of this study was to quantify the influence of zinc oxide nanoparticles (nanoZnO) on the water repellency and dimensional stability of beech wood. Beech wood blocks were treated with a nano-ZnO solution at four treatment levels (0, 10,000, 20,000, and 40,000 ppm) using a modified dip method. Also, a thermal treatment was performed at 60 and 120°C. After conditioning the samples, w...