An allomorph MnO₂@MnO₂ core-shell nanostructure was developed via a two-step aqueous reaction method. The data analysis of Scanning Electron Microscopy, Transmission Electron Microscopy, X-Ray Diffraction and N₂ adsorption-desorption isotherms experiments indicated that this unique architecture consisted of a porous layer of amorphous-MnO₂ nano-sheets which were well grown onto the surface of α...

The nucleation and growth mechanisms of porous MnO₂ coating deposited on graphite in MnSO₄ solution were investigated in detail by cyclic voltammetry, chronoamperometry and scanning electron microscopy. The electrochemical properties of honeycomb-like MnO₂ were evaluated by cycle voltammetry and galvanostatic charge-discharge. Results indicated that MnO₂ was synthesized by the following steps: ...

Here we explored a novel ZnO nanorod array template-assisted electrodeposition route to synthesize large-scale single-walled polypyrrole (PPy) nanotube arrays (NTAs) and multi-walled MnO(2)/PPy/MnO(2) NTAs. The structures of nanotubes, such as external and inner diameters, wall thicknesses, and lengths, can be well controlled by adjusting the diameters and lengths of ZnO nanorods and deposition...

Three kinds of MnO₂/Ni foam composite electrode with hierarchical meso-macroporous structures were prepared using potentiodynamic (PD), potentiostatic (PS), and a combination of PS and PD(PS + PD) modes of electrodeposition. The electrodeposition mode markedly influenced the surface morphological, textural, and supercapacitive properties of the MnO₂/Ni electrodes. The supercapacitive performanc...

We unprecedentedly report that layered MnO₂ nanosheets were in situ formed onto the surface of covalently bonded graphitic carbon nitride/reduced graphene oxide nanocomposite (g-C₃N₄/rGO), forming sheet-on-sheet structured two dimension (2D) graphitic carbon nitride/reduced graphene oxide/layered MnO₂ ternary nanocomposite (g-C₃N₄/rGO/MnO₂) with outstanding catalytic properties on thermal decom...

The formation mechanism of a coaxial manganese oxide/poly(3,4-ethylenedioxythiophene) (MnO(2)/PEDOT) nanowire is elucidated herein by performing electrodeposition of MnO(2) and PEDOT on Au-sputtered nanoelectrodes with different shapes (ring and flat-top, respectively) within the 200 nm diameter pores of an anodized aluminum oxide (AAO) template. It is found that PEDOT prefers to grow on the sh...

We consider the economics of the interaction between Mobile Virtual Network Operators (MVNOs) and Mobile Network Operators (MNOs). We investigate the incentives of an MNO for offering some of her resources to an MVNO instead of using the resources for her own End-Users (EUs). We consider a market with one MNO and one MVNO, and a continuum of undecided EUs. Two cases for EUs are considered: (i) ...

We demonstrate a facile, two-step coating/calcination approach to grow a uniform MnO nanoparticle@mesoporous carbon (MnO@C) composite on conducting substrates, by direct coating of the Mn-oleate precursor solution without any conducting/binding reagents, and subsequent thermal calcination. The monodispersed, sub-10 nm MnO nanoparticles offer high theoretical energy storage capacities and cataly...

Manganese oxide (MnO 2 ) microspheres are prepared using an ultrasonic spray pyrolysis (USP) process. A mixed solution of potassium permanganate and hydrochloric acid is nebulized into microsized droplets, which are then carried by air fl ow through a furnace tube. Each microdroplet serves as one microreactor and produces one microsphere. Upon heating, KMnO 4 is decomposed into MnO 2 microspher...

MnO nanoparticles have been tested to engineer a delayed increase in MRI T(1) relaxivity caused by cellular uptake via endocytosis into acidic compartments. Various coatings on core-shell structured MnO nanoparticles were tested for those that had the lowest T(1) relaxivity at pH 7.4, a pH where MnO does not dissolve into Mn(2+) ions. The rate of dissolution and release of Mn(2+) of the differe...