One of the most promising ways to produce a grain-refined microstructure in some steel materials is the thermomechanical processing route of subcritical recrystallization annealing of a cold-deformed martensite structure. In the present study, the microstructural evolutions and the associated recrystallization kinetics under various subcritical annealing heat treatment conditions are explored i...

Deformation behavior and microstructure evolution of NiTiCu shape memory alloy (SMA), which possesses martensite phase at room temperature, were investigated based on a uniaxial compression test at the temperatures of 700~1000 ◦C and at the strain rates of 0.0005~0.5 s−1. The constitutive equation of NiTiCu SMA was established in order to describe the flow characteristic of NiTiCu SMA, which is...

In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...

in this work dynamic recrystallization behavior of aisi 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 c -1200 c and strain rate range of 0.001 s-1 - 1 s-1. the obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. the flow stress and strain corresponding to the critical, pe...

The effect of austenite deformation on carbon partitioning and transformation to athermal isothermal martensite, bainite during quenching (QP) is described for three steel compositions: Fe-0.3C-0.6Si-1.1Al, Fe-0.3C-1.0Si Fe-0.3C-0.5Si-0.5Al. Microstructures were characterized using SEM-EBSD, TEM XRD. Austenite decomposition kinetics was investigated dilatometry. Deformation close the no-recryst...

The recrystallization behavior of cold-rolled, commercial-purity titanium was studied experimentally and with Monte-Carlo (MC) modeling. Utilization of EBSD-OIM as input for MC modeling resulted in realistic predictions of recrystallization kinetics, microstructure and texture, which were in good agreement with experimental results. MC modeling of recrystallization kinetics predicted that non-u...

In this work dynamic recrystallization behavior of AISI 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 C -1200 C and strain rate range of 0.001 s-1 - 1 s-1. The obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. The flow stress and strain corresponding to the critical, pe...

Tough pitch copper wire (99.97% Cu) is generally characterized by the spiral elongation number. The principle of the test is based on the influence of impurities on the recrystallization kinetics. Alternative non-metallographic techniques to characterize the recrystallization kinetics have been investigated in this study, such as differential scanning calorimetry (D.S.C.) and residual electrica...

Abstract With the aim of analyzing post-deformation Recrystallization (PDRX) 22MnB5 steel and grain size evolution after hot forming sheet using BAEHR 805 A/D thermo-mechanical simulator, several isothermal stress relaxation tests were performed in a temperature range 800 to 950 °C, predeformation 0.4 0.8 strain rate 0.01 s −1 . As result deformation, PDRX kinetics can be described based on an ...

A generalized phase transformation kinetics model is used to understand the martensite to austenite transformation in a cold-rolled and annealed metastable AISI 301LN ultrafine-grained austenitic stainless steel. The model shows that the presence of interstitial nitrogen and heavy cold-rolling is important to promote fast transformation kinetics, through rapid nitrogen-diffusion and austenite n...