the pseudo-elastic behavior of shape memory alloy (sma) truss and cantilever beam are investigated. brinson’s one-dimensional material model, which uses the twinned and detwinned martensite fractions separately as internal variables, is applied in the algorithm to establish the sma stress-strain characteristics. this material model also incorporates different young’s modulus for austenitic and ...

dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500c. stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500c, and smooth flow at the other temperatures. both yield and ultimate tensile strengths increased with increasing testing temperature up to about 4500c and then decreased at h...

The strength of mixed microstructures of bainite and martensite can peak at an intermediate volume fraction of martensite has been published by recently experimental studies. A quantitative interpretation of these observations is achieved by modelling the mechanical properties of mixed microstructures of bainite and martensite. The peak in the curve of the strength as a function of the volume f...

Deformation and work hardening behavior of Fe-17Mn-0.02C steel containing ε-martensite within the austenite matrix have been investigated by means of in situ microstructural observations and x-ray diffraction analysis. During deformation, the steel shows the deformation-induced transformation of austenite → ε-martensite → α'-martensite as well as the direct transformation of austenite → α'-mart...

Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...

Strain-induced phase transformation and damage accumulation in austenitic stainless steel subjected to cyclic loading were investigated by nondestructive evaluation. The cyclic loading test was performed at various strain amplitudes at the same strain rate. The volume fraction of the strain-induced phase transformation (α′-martensite) was determined by ferrite scope and magnetic coercivity meas...

Mechanical properties of machined components are controlled by inducing phase transformations in the outer layer of the materials. Induction hardening is one such manufacturing process where the surface hardness is enhanced while the core is retained with the original structure and characteristics. In this study, a mathematical model had been developed to predict the hardness and the volume fra...

Many studies monitoring the formation of martensite during the tensile deformation of austenite report data which are, in principle, affected by both the applied stress and the resulting plastic strain. It is not clear in these circumstances whether the transformation is stress induced (i.e. the stress provides a mechanical driving force) or whether the generation of defects during deformation ...