polycrystalline mfi zeolite membranes were prepared on α-alumina tubular support by hydrothermal treatments at 413 k. the synthesized zeolite membranes were characterized by xrd, sem and single gas permeation. the influence of hydrothermal treatment steps and the calcination time on the zeolite layer formation were investigated. mfi zeolite membrane prepared by four subsequent hydrothermal trea...

hydrothermal treatment of wood material products with many interesting properties such as enhanced dimensional stability, lower equilibrium moisture content and increased biological durability. the effects of hydrothermal treatment on dimensional stability, oven dry density and water absorption of beech wood (fagus orientalis) naturally grown, has been studied in present research that extremely...

Hydrothermal treatment of wood material products with many interesting properties such as enhanced dimensional stability, lower equilibrium moisture content and increased biological durability. The effects of hydrothermal treatment on dimensional stability, oven dry density and water absorption of beech wood (Fagus Orientalis) naturally grown, has been studied in present research that extremely...

Polycrystalline MFI zeolite membranes were prepared on α-alumina tubular support by hydrothermal treatments at 413 K. The synthesized zeolite membranes were characterized by XRD, SEM and single gas permeation. The influence of hydrothermal treatment steps and the calcination time on the zeolite layer formation were investigated. MFI zeolite membrane prepared by four subsequent hydrothermal ...

molecular sieves and zeolites are materials whose crystalline frameworks form nanometer or subnanometer pores. a variety of different crystal structures are known having a range of pore sizes. because the pore sizes are usually smaller than 2 nm, they are classified as microporous materials. synthesis of microporous materials is usually conducted by the high temperature treatment (80-200 °c) of...

zeolite was synthesized from coal tailings and coal fly ash sampled from zarand coal washing plant, iran, using h2o2–promoted hydrothermal treatment. samples consisted mainly of sio2 and al2o3 which are the main components for the zeolite synthesis. to perform the experiments, appropriate amount of the starting materials were mixed with 240 ml volume of 30% h2o2 at room temperature with continu...

Molecular sieves and zeolites are materials whose crystalline frameworks form nanometer or subnanometer pores. A variety of different crystal structures are known having a range of pore sizes. Because the pore sizes are usually smaller than 2 nm, they are classified as microporous materials. Synthesis of microporous materials is usually conducted by the high temperature treatment (80-200 °C) of...

Molecular sieves and zeolites are materials whose crystalline frameworks form nanometer or subnanometer pores. A variety of different crystal structures are known having a range of pore sizes. Because the pore sizes are usually smaller than 2 nm, they are classified as microporous materials. Synthesis of microporous materials is usually conducted by the high temperature treatment (80-200 °C) of...

Anhydrite (CaSO4) is a major component of evaporitic rocks and is currently forming in submarine hydrothermal fields, where its dissolution and precipitation plays a significant role in controlling porosity. Anhydrite also is a component of undesirable scale on heat transfer surfaces during desalinization and waste water treatments. Knowledge of the molecular processes that control anhydrite gr...