In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...

in this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from isfahan steel mill for cement. the control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. the slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...

In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...

Hybrid Concrete focused on the development of buildings, highways, and other structures of civil engineering. In the current study, various mix combinations have been prepared and tested with different percentages of super-plasticizer at different levels of water reduction for obtaining the optimum mix. Further, study on different properties of hybrid concrete and replacement of ordinary portla...

The replacement of natural resources in the manufacture of cement and sand is the present issue in the present construction scenario. Copper slag and Ground Granulated Blast furnace Slag (GGBS) are industrial by-product materials produced from the process of manufacturing copper and iron. Use of Copper slag and GGBS does not only reduce the cost of construction but also helps to reduce the impa...

the marble slurry wastes (msw) produced by marble industry is left unattended in theenvironment which causes serious environmental problems. in order to evaluate its potential usage in normal1:2:4 concrete, this study was designed, where the partial replacement of cement with msw was examined.replacement of cement with msw from 0 to 100%, and also its usage as an additive material 10% and 20% b...

Cement manufacturing industry is one of the carbon dioxide emitting sources besides deforestation and burning of fossil fuels. The global warming is caused by the emission of green house gases, such as CO2, to the atmosphere. Among the greenhouse gases,CO2 contributes about 65% of global warming. The global cement industry contributes about 7% of greenhouse gas emission to the earth’s atmospher...

The aim of this study is to investigate the feasibility of using waste bricks powder of Gachsaran Company in concrete. Cement is replaced by waste bricks powder in different proportions until 40 percent by weight. pozzolanic properties of bricks powder and compressive strength of concrete were investigated. The results demonstrated that the bricks powder show pozzolanic properties. Results also...