This paper aims to clarify the effect of steel fiber on the flexural toughness of the high performance concrete containing fly ash and nano-SiO2. The flexural toughness was evaluated by two methods, which are based on ASTM C1018 and DBV-1998, respectively. By means of three-point bending method, the flexural toughness indices, variation coefficients of bearing capacity, deformation energy, and ...

PURPOSE The aim of this study was to clarify the effect of addition of glass fibers and titanium dioxide nanoparticles to the conventional acrylic resin. The tested parameters were monomer release, deflection at fracture, flexural strength, flexural modulus, and toughness. The modified acrylic resin groups were compared to the conventional unmodified and high impact types. The correlation betwe...

Mortars containing carbon, polyethylene, and stainless steel fibers at the same volume fraction and with similar fiber diameters were compared in terms of tensile, compressive, and flexural properties. Carbon fibers, though having the lowest tensile modulus, stren[?th, and elongation at break among the fiber types, [?ave mortar of the highest tensile strenf?th and lowest cost; polyethylene fibe...

in this study the effect of using multi-walled carbon nanotube (mwcnt) on flexural and compressive strengths, ultimate displacement and energy absorption capability of standard cement mortar considering different weight percentages of nanotubes as well as different dispersion methods has been investigated. influential point in adding nanotubes to the composites is their proper dispersion, which...

. AbstrAct Objective. In clinical practice, core material can be exposed after adjustments, which may result in loss of ceramic glaze. The objective of this study is to evaluate the effect of surface roughness on the flexural strength and fracture toughness of In-Ceram zirconia core material. Materials and methods. Forty In-Ceram zirconia specimens were prepared and divided into two main groups...

We evaluated the effect of water storage on fluoride release and mechanical properties of compomer restorative material. Fluoride release was recorded using a specific fluoride electrode. Flexural properties and fracture toughness were measured using a universal testing machine. Vickers hardness was measured using a micro-hardness tester. There was initial burst of fluoride release up to 1 w, w...

Purpose: The mechanical strength of polymethyl methacrylate (PMMA) remains far from ideal for maintaining the longevity of denture. The purpose of this study was to evaluate the effect of Zirconium oxide (ZrO2) nanofillers powder with different concentration (1.5%, 3%, 5% and 7%) on the flexural strength, fracture toughness, and hardness of heat-polymerized acrylic resin. Materials and methods:...

The aim of the present study was to measure various mechanical properties of acrylic denture base resins, including flexural modulus, flexural strength, fracture toughness, Barcol and Vickers hardness and their related properties, and to investigate correlations between different mechanical properties. Resin specimens were prepared according to manufacturers' recommended instructions. The mecha...

The aim of this study was to investigate the flexural behavior of engineered cementitious composites (ECCs) reinforced by cellulose pulp (CP) and cellulose microfibers (CMF). The reinforcements were obtained from chemical-mechanical treatments of Kraft paper and used in ECC mix design. Results showed that cement reinforced by CP exhibited a strain-hardening behavior in the three-point bending t...

INTRODUCTION Prolonged exposure of root dentin to calcium hydroxide alters the fracture resistance of dentin. Calcium silicate-based materials (CSMs) used in endodontics release calcium hydroxide on setting. This study examined whether prolonged contact of dentin with CSMs adversely affects its mechanical properties. METHODS Dentin beams prepared from extracted human molars (7 × 3 × 0.3 mm) w...