to investigate and compare the amount of fluoride release of conventional, resin modified and nanofilled resin modified glass ionomer cements.tablets of glass-ionomer cements were immersed in deionized water and incubated at 37°c. after 1, 2, 7, 15 and 30 days, fluoride ion was measured under normal atmospheric conditions by fluoride ion selective electrode. buffer (tisab ii) was used to decomp...

OBJECTIVE This in vitro study evaluated the microleakage of a nano-filled resin-modified glass ionomer and a high viscosity glass-ionomer restorations in class V cavities. MATERIALS AND METHODS Thirty-two class V cavities prepared on the buccal and lingual surfaces of 16 sound, third molar teeth were randomly assigned into two groups and restored by one of the glass ionomer material; Group A:...

Objective: The Purpose of this investigation was to assess the effectiveness of Mineral Trioxide Aggregate in providing an apical seal in comparison with High Copper Silver Amalgam, Conventional Glass Ionomer Cement Type 2, and Glass Cermet cement by using a dye penetration method. Methods: The root canals of seventy extracted teeth were instrumented and obturated with gutta-percha. Each tooth ...

Glass ionomer cements (GICs) are widely used in restorative dentistry.1 In dentistry, one of their advantages over other restorative materials is that they can be placed into tooth cavities without an additional bonding agent.2 They also possess a fluoride-releasing property3 and are relatively biocompatible with the pulp.1 Adhesive property and fluoride release of glass ionomer cement contribu...

statement of problem: despite the wide range of new dental materials, there is still a need for biomaterials demonstrating high biocompatibility, antimicrobial effects and ideal mechanical properties. purpose: the aim of this study was to histologically evaluate the pulpal response to a conventional glass ionomer, a resin modified glass ionomer and a calcium hydroxide in human teeth. materials ...

OBJECTIVE The aim of this study was to investigate the adaptation of different types of restorations towards deciduous and young permanent teeth. MATERIAL AND METHODS Class V cavities were prepared in deciduous and young permanent teeth and filled with different materials (a conventional glass-ionomer, a resin-modified glass-ionomer, a poly-acid-modified composite resin and a conventional com...

polymerization contraction may produce defects in the composite - tooth bond. this may lead to bond failure and microleakage. the aim of this study was to reduce microleakage of posterior composites using different methods. 45 molar and premolars extracted teeth were choosen. the cavities were randomly assigned into 5 groups of 9. box-shaped cavities were prepared on each side of proximal surfa...

The purpose of this study was to evaluate the disintegration of luting agents. An intraoral sample holder was made having four holes of 1.4 mm diameter and 2 mm depth. The holder was soldered onto the buccal surface of an orthodontic band, which was cemented to the first upper molar in 12 patients, average age 26 years. The holes were filled with a zinc phosphate (Phosphate Kulzer), a glass ion...