Fatigue crack growth is examined in P/M 2124 aluminum alloys reinforced with SiC particles (SiCp) and whiskers (SiCw) over a wide spectrum of growth rates from 10 to 10 m per cycle. Effects of aging treatment, orientation of crack growth direction with respect to the rolling direction, mean stress (or stress ratio), and reinforcement volume percent on the fatigue crack growth threshold are inve...

effect of partial natural rubber replaced with synthetic rubbers, styrene butadiene and cis butadiene, on failure and strength properties of bias tread nr/br based compound was studied by efficient and conventional sulfur curing systems and mixtures of different carbon black grades. it was observed that failure behavior comprising tear resistance and crack growth in substituted compounds droppe...

the blending of nr and br rubber blend with n330 carbon black is studied on curing behavior and the physico-mechanical properties of a sbr rubber based tire tread compound containing n234 carbon black. the effect of sulphur and accelerator contents on different properties of rubber compound is also tested with a wide range of curing agents. partial substitution of sbr with nr shows significant ...

Fatigue crack initiation and early short crack propagation behaviour in two microstructural variants of a recently developed Low Solvus, High Refractory (LSHR) disc superalloy at room temperature has been investigated by three-point bending with replication procedure. The results shows that fine gained (FG) LSHR possesses higher fatigue life due to its better crack initiation resistance, limite...

A study has been made of the fatigue-crack propagation properties of a series of laminated Nbreinforced Nb3Al intermetallic-matrix composites with varying microstructural scale but nominally identical reinforcement volume fraction (20 pct Nb). It was found that resistance to fatigue-crack growth improved with increasing metallic layer thickness (in the range 50 to 250 mm) both in the crack-divi...

In this study, 5052 Al–Mg alloy was pre-treated and friction stir processing (FSP) was then performed on the specimens to explore the deformation resistance. The experimental results indicate that the FSP specimens not only had better tensile properties but also better vibration fracture resistance. It is significant that the tensile elongation and deformation resistance tended to increase as t...

Fracture toughness resistance curves describe a material's resistance against crack propagation. These curves are often used to characterize biomaterials like bone, nacre or dentin as these materials commonly exhibit a pronounced increase in fracture toughness with crack extension due to co-acting mechanisms such as crack bridging, crack deflection and microcracking. The knowledge of appropriat...

This study evaluated the tradeoffs amongst fatigue crack propagation resistance, wear resistance, and oxidative stability in a wide variety of clinically-relevant cross-linked ultra-high molecular weight polyethylene. Highly cross-linked re-melted materials showed good oxidation and wear performance, but diminished fatigue crack propagation resistance. Highly cross-linked annealed materials sho...

The propagation of cracks in graded materials under monotonic and cyclic loading was investigated via experiment and simulation. Graded alumina/epoxy composite specimens exhibiting a variation in composition from 5% to 65% epoxy, representing a twenty-fold variation in Young’s modulus, across a region of width between 6 and 20 mm, were produced by a multistep infiltration technique. Crack initi...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...