in this research, the decay resistance of bagasse-polypropylene composite has been evaluated. the scope of research was to assess the effect of different weight percentages of bagasse (40, 55 and 70%) and coupling agent, (mapp) maleic anhydride grafted polypropylene (0, 4 and 6%) on the fungal decay of the composite. astm d1413-99 modified test method was used to carry out the decay test, trame...

this work investigates the feasibility of using recycled high density polyethylene (rhdpe), recycled polypropylene (rpp) and old newsprint fiber (onp) to manufacture fiber reinforced composites. the boards were made through air-forming and hot press. the effects of the fiber loading and coupling agent content on tensile, flexural, internal bond properties and water absorption and thickness swel...

in this research, the possibility of using high percentage of lignocellulosic fibers in making natural fiber-thermoplastic composite was studied. three weight percentages of bagasse flour namely 40, 55 and 70 percents were chosen. mapp was used as coupling agent at two weight percentages of pp, namely 0, 4 and 6 percents. tensile strength was measured applying instron 6025. the results showed t...

tobacco is planted extensively in golestan province and high volume of its stem wastes remained without using and it is burned. as a useful purpose of these wastes and to reduce the environmental problems, in this the mechanical properties of polypropylene composites reinforced with tobacco stalk flour were studied. for this purpose, the tobacco stalk flour as the reinforcement, in three levels...

zinc oxide nano-particles with the average diameter of about 25 nm were modified with different mole ratios of trimetoxyvinyl silane (tmvs) and oleic acid, as coupling agents, in order to modify their surface properties and render them more hydrophobic. then, dispersibility of the surface modified nano-particles was examined in some monomers with different levels of hydrophobicity, including me...

Titanium dioxide (TiO2) nanoparticles, with an average size of about 45 nm, were encapsulated by polystyrene using in situ nitroxide mediated radical polymerization   in the presence of 3-aminopropyl triethoxy silane (APTES) as a coupling agent and 2, 2, 6, 6-tetramethylpiperidinyl-1-oxy  as a initiator. First, the initiator for NMRP was covalently bonded onto the surface of Titanium dioxide na...

Zinc oxide nano-particles with the average diameter of about 25 nm were modified with different mole ratios of trimetoxyvinyl silane (TMVS) and oleic acid, as coupling agents, in order to modify their surface properties and render them more hydrophobic. Then, dispersibility of the surface modified nano-particles was examined in some monomers with different levels of hydrophobicity, including me...

Zinc oxide nano-particles with the average diameter of about 25 nm were modified with different mole ratios of trimetoxyvinyl silane (TMVS) and oleic acid, as coupling agents, in order to modify their surface properties and render them more hydrophobic. Then, dispersibility of the surface modified nano-particles was examined in some monomers with different levels of hydrophobicity, including me...

titanium dioxide (tio2) nanoparticles, with an average size of about 45 nm, were encapsulated by polystyrene using in situ nitroxide mediated radical polymerization   in the presence of 3-aminopropyl triethoxy silane (aptes) as a coupling agent and 2, 2, 6, 6-tetramethylpiperidinyl-1-oxy  as a initiator. first, the initiator for nmrp was covalently bonded onto the surface of titanium dioxide na...

background: bonding of molar tubes is becoming more popular in orthodontics. occasionally, these bonding are done on posterior porcelain crowns or bridges. the purpose of this study was to evaluate the shear bond strength of buccal tubes on feldspathic porcelain crowns with two different methods. materials and methods: forty porcelain right molar crowns were fabricated for this study. the crown...