2013
A. K. Mukherjee

The various mechanisms that have been put forward to explain stress-corrosion cracking are briefly summarized. The experimental observations of stress-corrosion cracking in titanium alloys in widely different environmer a are discussed. Evidence from the literature for and against the possibility that hydrogen plays a role in the stress-corrosion cracking of titanium alloys is documented. An ex...

2016
Lei Wang Lizhao Dai Xuhui Zhang Jianren Zhang

The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracki...

1998
R. D. Kane

Hydrogen sulfide (H$) has long been associated with the cause of corrosion damage and sulfide stress cracking (SSC) in high strength steels and high hardness weldments used in oil and gas production, petroleum refining, and petrochemical/chemical processing. Other applications where sulfide species have produced environmental cracking include heavy water production, electric power, marine appli...

2016
Jianghong Mao Fang-Yuan Xu Qian Gao Sheng-lin Liu Weiliang Jin Yidong Xu

Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology ...

2016
Jianfeng Dong Yuxi Zhao Yingyao Wu Weiliang Jin

A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...

2016
S. D. Wang D. K. Xu B. J. Wang L. Y. Sheng E. H. Han C. Dong

Effect of solid solution treatment (T4) on stress corrosion cracking (SCC) behavior of an as-forged Mg-6.7%Zn-1.3%Y-0.6%Zr (in wt.%) alloy has been investigated using slow strain rate tensile (SSRT) testing in 3.5 wt.% NaCl solution. The results demonstrated that the SCC susceptibility index (ISCC) of as-forged samples was 0.95 and its elongation-to-failure (εf) was only 1.1%. After T4 treatmen...

2012
Mitsuharu Shiwa Hiroyuki Masuda Hisashi Yamawaki Kaita Ito Manabu Enoki

Acoustic emission with near-field detection and optical video microscope monitoring was proposed to investigate the pitting corrosion caused by a small magnesium-chloride droplet. Four types of the detected waveforms were characterized by the wavelet analysis to investigate the corrosion of work-hardened SUS304 stainless steel. After high-activity AE signals observed, the corrosion product shee...

2015
Jianghong Mao Jiayun Chen Lei Cui Weiliang Jin Chen Xu Yong He

Expansion and cracking induced by the corrosion of reinforcement concrete is the major factor in the failure of concrete durability. Therefore, monitoring of concrete cracking is critical for evaluating the safety of concrete structures. In this paper, we introduce a novel monitoring method combining Brillouin optical time domain analysis (BOTDA) and fiber Bragg grating (FBG), based on mechanic...

2017
Marina Cabrini Sergio Lorenzi Tommaso Pastore Simone Pellegrini Mauro Burattini Roberta Miglio

The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens eithe...

2007
M. J. S. Lowe P. Cawley

Guided wave inspection of pipelines is now in routine use worldwide. The technique offers the possibility of rapid screening of long lengths of pipework for corrosion and other defects. A test range of 50m or more (25m in each direction) is commonly obtained from a single transducer position. Long range guided wave inspection techniques are also in development for several other applications, in...