the structural and electrical properties of polyaniline-cobalt sulphate nanocomposite prepared by chemical method.polyaniline-cobalt sulphate nanocomposites were synthesized by the cobalt sulphate and ammonium persulphate and aniline.this paper reports on chemical technique using for synthesis of cobalt nanoparticles in the composite bridge is aniline. electrical conductivity of polyaniline wit...

Cobalt oxide (Co3O4) nanoparticles were successfully prepared by thermal decomposition of cobalt hydroxide synthesized from cobalt acetate, ammonium hydroxide and 10% glycerol. The cobalt oxide nanoparticles calcined at 450 °C were characterized by using XRD. The XRD confirms the crystallinity and crystal structure of the sample. It also shows that the diffraction peak are broadened which revea...

Silica nanoparticles were directly coated with cobalt hydroxide by homogeneous precipitation of slowly decomposing urea in cobalt nitrate solution. The cobalt hydroxide was amorphous, and its morphology was nanoflower-like. The BET (Brunauer-Emmett-Teller) surface area of the core-shell composite was 221 m²/g. Moreover, the possible formation procedure is proposed: the electropositive cobalt io...

Monodisperse cobalt nanoparticles are synthesized via a high-temperature thermal decomposition method in the presence of oleic acid and triphenylphosphine. The as-synthesized nanoparticles are stable against further deep oxidation when they are kept in heptane .C7H16/. Time-dependent XPS studies indicate that oxidation of the as-synthesized cobalt nanoparticles in air is slow. The valence chang...

Cobalt-doped iron oxide nanoparticles were prepared by solution combustion technique. The structural and magnetic properties of the prepared samples were also investigated. The average crystallite size of cobalt ferrite (CoFe2O4) magnetic nanoparticle was calculated using Scherrer equation, and it was found to be 16±5 nm. The particle size was measured by transmission electron microscope. This ...

In situ soft X-ray absorption spectroscopy (XAS) was employed to study the adsorption and dissociation of carbon monoxide molecules on cobalt nanoparticles with sizes ranging from 4 to 15 nm. The majority of CO molecules adsorb molecularly on the surface of the nanoparticles, but some undergo dissociative adsorption, leading to oxide species on the surface of the nanoparticles. We found that th...

We report the preparation of a new type of nanocomposite containing cobalt and silver nanoparticles organized in parallel layers with a well controlled separation. This arrangement allows the observation of an enhanced low-frequency Raman signal at the vibration frequency of cobalt nanoparticles excited through the surface plasmons of silver nanoparticles. Numerical simulations of the electric ...

Core-shell magnetic nanoparticles have received significant attention recently and are actively investigated owing to their large potential for a variety of applications. Here, the synthesis and characterization of bimetallic nanoparticles containing a magnetic core and a gold shell are discussed. The gold shell facilitates, for example, the conjugation of thiolated biological molecules to the ...

Recent advances in the synthesis of various magnetic nanoparticles using colloidal chemical approaches are reviewed. Typically, these approaches involve either rapid injection of reagents into hot surfactant solution followed by aging at high temperature, or the mixing of reagents at a low temperature and slow heating under controlled conditions. Spherical cobalt nanoparticles with various crys...

The fabrication of carbon-shell protected cobalt nanoparticles and hollow graphitic shells has been achieved via a pyrolysis process by using monodispersed cobalt nanoparticles as a template. These materials are mesoporous and highly stable under strong acidic and basic conditions.