Nano-TiO2 (NT) and nano-SiO2 (NS) were separately added in the cement paste to investigate the rheological property of fresh mixtures and mechanical strength in hardened state. The effects of different dosages and types of nano-particles on the properties of cement paste were studied. The results indicated that the rheological behavior of the fresh cement paste coincides with the Modified Bingh...

Carbon nanotubes (CNTs) have excellent mechanical properties and can be used to reinforce cement-based materials. On the other hand, the reaction product of carbonation with hydroxides in hydrated cement paste can reduce the porosity of cement-based materials. In this study, a novel method to improve the strength of cement paste was developed through a synergy of carbon nanotubes decorated with...

The influences of nano-ZrO2 (NZ), nano-TiO2 (NT), nano-Fe2O3 (NF) and nano-Al2O3 (NA) additions on properties of the fresh and hardened cement paste in comparison with the fine cement paste were experimentally studied. Mini slump and flow cone tests were conducted on fresh cement pastes. Moreover the compressive and tensile strength of hardened cement paste were measured. SEM micrographs and XR...

In this paper, we describe the monitoring of Portand cement paste, with a 0.50 water cement ratio (w/c), during early age period, recurring to optical and electrical techniques. The optical monitoring of the cement paste was realized with FBG temperature sensors, and the temperature variations during the early age period were characterized. The RF values of the cement paste and therefore predic...

The effect of a short heat treatment on hydrated cement paste has been investigated by measuring the weight and length changes of specimens as they undergo various combinations of heating, drying, and resaturation. Heating a cement paste to 60°C coarsens the capillary pore system, decreases the volume of mesopores, and increases the degree of polymerization of the silicates. In addition, the sa...

A Hysitron Triboindenter has been used to determine the mechanical properties of hardened cement paste and cement paste at the early age. This technique provides an in-situ scanning probe microscopy (SPM) imaging facility that allows pre and post-test observation of the sample. The same probe is used to indent and image eliminating the complicated situation of locating the same area with differ...

The data presented herein are compiled of the research summary of "Staple-wire-reinforced high-volume fly-ash cement paste composites" (Aydin, in preparation) [1]. This data article provides general information about the novel high volume fly ash cement paste composites composed of various volume of staple wires. The dataset here also helps the readers to understand the mechanisms of staple wir...

This research investigates changes in the nanostructure and the nanoscale local mechanical properties of cement paste with microand nano-modifiers. Silica fume and multiwall carbon nanotubes (MWCNTs) were used as microand nano-modifiers. An effective method of dispersing CNTs in cement matrix was developed. A detailed study on the effects of CNTs concentration and aspect ratio on the fracture p...

A method for producing radio-wave-reflecting concrete, which is potentially useful for lateral guidance in automatic highways, is provided. In the form of cement paste, it contains a small amount (0.5 vol.%) of 0.1 mm diameter carbon filaments as an admixture. The radiation absorbed is negligible compared to that reflected. The reflectivity at 1 GHz is 10 dB higher for radiowave-reflecting ceme...

Microencapsulated phase-change materials (MPCM) can be used to develop a structural-functional integrated cement paste having high heat storage efficiency and suitable mechanical strength. However, the incorporation of MPCM has been found to degrade the mechanical properties of cement based composites. Therefore, in this research, the effect of carbon nanotubes (CNTs) on the properties of MPCM ...