The efficiency of Co(II)-, Mn(II)-, and Ti(IV)-doped carbon aerogels for the transformation of ozone into (*)OH radicals was investigated. The carbon aerogels had a markedly acid surface character (pH(PZC approximately equal) congruent with 3-4) with very high surface oxygen concentrations (O approximately equal with 20%). X-ray photoelectron spectroscopy (XPS) analyses of the samples showed th...

A carbon aerogel was obtained by carbonization of an organic aerogel prepared by sol-gel polymerization of resorcinol and formaldehyde in water. The carbon aerogel was then CO(2) activated at 800 degrees C to increase its surface area and widen its microporosity. Evolution of these parameters was followed by gas adsorption and small- and wide-angle X-ray scattering (SAXS and WAXS, respectively)...

The fabrication of supercapacitor electrodes with high energy density and excellent cycling stability is still a great challenge. A carbon aerogel, possessing a hierarchical porous structure, high specific surface area and electrical conductivity, is an ideal backbone to support transition metal oxides and bring hope to prepare electrodes with high energy density and excellent cycling stability...

The presented paper contains a brief review on the synthesis and characterization of silica aerogels and its nanocomposites with nanofibers and fibers based on a literature study over the past twenty years and my own research. Particular attention is focused on carbon fiber-based silica aerogel nanocomposites. Silica aerogel is brittle in nature, therefore, it is necessary to improve this drawb...

Introduction Carbon aerogel (CA) is a most promising material as an electrode for electrical double-layer capacitor (EDLC), as it allows an interconnected three-dimensional network structure, a high specific surface area, good electrical conductivity and a suitable pore size distribution for common electrolytes. Moreno-Castilla et al. [1] prepared titania/carbon composite by the sol-gel method,...

5-methylresorcinol and the technical mixture of oil-shale phenolic compounds were applied for carbon aerogel preparation. Gels, which were prepared via base catalyzed polymerization were dried under supercritical conditions and subsequent pyrolysis of obtained dry aerogels led to carbon aerogels. Activation of carbon aerogel with CO2 and H2O was performed and porosity and the specific surface a...

Biomass is the most plentiful and well-utilized renewable carbon resource on the earth. Direct conversion of biomass to carbon aerogel provides a promising approach to develop adsorbent materials. In the present work, the effect of presence of water during hydrothermal treatment and holding temperature during post-pyrolysis process have been investigated for the preparation of carbon aerogels (...

A flexible carbon fiber aerogel with a very high surface area for supercapacitor application is reported by carbonization and chemical activation of low-cost natural cotton with KOH. The carbon fibers in the aerogel present as a twisted and tubular structure. Depending on the amount of KOH used in the activation process, the specific surface area of aerogels ranges from 1536 to 2436 m g−1, whil...

Current applications of carbon-based supercapacitors are limited by their low energy density. One promising strategy to enhance the energy density is to couple metal oxides with carbon materials. In this study, a porous MnCo2O4.5 nanoneedle/carbon aerogel hybrid nanostructure was synthesized by assembling MnCo2O4.5 nanoneedle arrays on the surface of channel walls of hierarchical porous carbon ...

This article reports measurements of the concentration distribution of two model proteins adsorbed from aqueous solution by two different high surface area carbons, using small angle neutron and X-ray scattering (SANS and SAXS). The proteins investigated were bovine serum albumin (67 kDa), and bovine pancreatic trypsin inhibitor (BPTI), also known under the name aprotinin (6.5 kDa). The two car...