A bench work study was carried out to investigate the use of kaolinitic clay containing 29.4% Al2O3 extremely abundant in Saudi Arabia for the production of pure alumina by calcination at 700 o C for 1h (recommended by previous investigators) then leached by hydrochloric acid. The effects of leaching temperature (25 o C to boiling temperature), period of activation (10-150 minutes), acid concen...

Nickel-induced morphology change of mesostructured alumina with amorphous walls to bayerite tetrahedra when treated in water, and then to γ-alumina with worm-like mesopores topologically after it was calcined at 400 °C is reported. The catalytic activity for selective CO methanation increased significantly after this treatment.

Selecting a proper support in the catalyst system plays an important role in hydrogen production via ethanol steam reforming. In this study, sol gel made alumina supports prepared for nickel (Ni) catalysts were calcined at different temperatures. A series of (Ni/AlS.G.) catalysts were synthesized by an impregnation procedure. The influence of varying the calcination temperature of the sol gel m...

Samples containing mixtures of 5 mol % La203 and 95 mol % Al203 were prepared by homogeneous precipitation method with or without the presence of various anions, and calcined at different temperatures in the range of 873-1473 K. Sample prepared by urea hydrolysis in the absence of anions, and calcined at about 1273 K results in the formation of pure lanthanum-,8-alumina (LBA) with high surface ...

Alumina nanofibers were prepared by a technique that combined the sol-gel and electrospinning methods. The solution to be electrospun was prepared by mixing aluminum isopropoxide (AIP) in ethanol, which was then refluxed in the presence of an acid catalyst and polyvinylpyrolidone (PVP) in ethanol. The characterization results showed that alumina nanofibers with diameters in the range of 102 to ...

aluminum sulfate nano structures have been prepared by solution combustion synthesis using aluminum nitrate nonahydrate (al(no3)3.9h2o) and ammonium sulfate ((nh4)2so4). the resultant aluminum sulfate nano structures were calcined at different temperatures to study thermal  decomposition of aluminum sulfate. the crystallinity and phase of  the as-synthesized and calcined samples were characteri...

The paper reports a process for synthesis of γ-alumina from kaolin. Kaolin was transformed to meta-kaolin by calcination at 800 ̊C for 2h. γ-alumina powder was synthesized through extracting alumina from metakaolin via H2SO4 and meta-kaolin reactions and consequently precipitation in ethanol, which led to form the aluminum sulfate. The precipitated aluminum sulfate was dried and calcined at 900 ̊...

Homogeneous distribution of mullite in the matrix of alumina can be obtained through sol-gel method. In this work, nanopowder of alumina-mullite composite was synthesized with high homogeneity and high purity. So aluminum chloride hexahydrate and tetraethyl orthosilicate were used instead of alumina or mullite nanopowder. Studying the simultaneouse thermal analysis (STA) of mullite precursor re...

Aluminum sulfate nano structures have been prepared by solution combustion synthesis using aluminum nitrate nonahydrate (Al(NO3)3.9H2O) and ammonium sulfate ((NH4)2SO4). The resultant aluminum sulfate nano structures were calcined at different temperatures to study thermal  decomposition of aluminum sulfate. The crystallinity and phase of  the as-synthesized and calcined samples were char...

A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic Separation and leaching with HCl and chemical bleaching treatment by using sodium dithionite (Na 2 S 2O4 ) as reducing agent in acidic media (H 2SO 4 ) were used. Pur...