The influence of a minor strontium (Sr) modifier on the microstructures and mechanical properties of 7075 Al alloys was investigated in this paper. The grain size of cast 7075 Al alloys was refined from 157 μm to 115 μm, 108 μm, and 105 μm after adding 0.05 wt. %, 0.1 wt. %, and 0.2 wt. % Sr, respectively. The extruded 7075 Al alloys was refined with different degrees of Sr modifier. The mechan...

In this study, age hardenable material Aluminum alloy Al-7075-T6 (aged) was investigated for weldability. Al-7075-T6 plates were subjected to Al-7075-0 heat treatment and were joined with different welding parameters by means of friction stir welding method. After Joining, the parts which were subjected to tensile and bending tests were examined. As a result of the studies, it was observed that...

In the present study, an attempt has been made to investigate the influence of the forging parameters on cutting forces for different cutting speed, depth of cut, and feed rate during machining of Al 7075 alloy and Al 7075 alloy with short basalt fiber reinforced metal matrix composites. The experiments were conducted by using a lathe machine with tool dynamometer setup. KeywordForging effect, ...

The nucleation undercooling of TiB₂/7075 Al matrix composites, the microstructure observed after solidification at different cooling rate, and the size and distribution of TiB₂ particles were investigated. The experimental results have shown that the grain sizes of TiB₂/7075 Al matrix composites firstly decreased, then increased, and finally decreased again with the increase of TiB₂ content. Th...

The present study was undertaken to investigate the effect of pre-aging and aging parameters (time and temperature) on the mechanical properties of Al-Mg-Zn (7075) alloys. Ultimate tensile strength, 0.5% offset yield strength and % elongation measurements were carried out on specimens prepared from cast and heat treated 7075 alloys. Aging treatments were carried out for the as solution treated ...

The present study was undertaken to investigate the effect of pre-aging and aging parameters (time and temperature) on the mechanical properties of Al-Mg-Zn (7075) alloys. Ultimate tensile strength, 0.5% offset yield strength and % elongation measurements were carried out on specimens prepared from cast and heat treated 7075 alloys. Aging treatments were carried out for the as solution treated ...

The failure response of aluminum alloys (Al-6061 and Al-7075) under the condition of simultaneously pre-stressing and laser heating was investigated. Specimens were subjected to predetermined preloading states and then irradiated by continuous wave fiber (Yb) laser. For all specimens, it was found that the yield stress decreased with increasing laser power density. This implies that the load-be...

To provide insight into the relationships between precipitation phenomena, grain size and mechanical behavior in a complex precipitation-strengthened alloy system, Al 7075 alloy, a commonly used aluminum alloy, was selected as a model system in the present study. Ultrafine-grained (UFG) bulk materials were fabricated through cryomilling, degassing, hot isostatic pressing and extrusion, followed...

The present study was undertaken to investigate the effect of aging parameters (time and temperature) on the mechanical properties of Be-and/or Zrtreated Al-Mg-Zn (7075) alloys. Ultimate tensile strength, 0.5% offset yield strength and % elongation measurements were carried out on specimens prepared from cast and heat treated 7075 alloys containing Be and/or Zr. Different aging treatment were c...

The present study was undertaken to investigate the effect of aging parameters (time and temperature) on the mechanical properties of Be-and/or Zrtreated Al-Mg-Zn (7075) alloys. Ultimate tensile strength, 0.5% offset yield strength and % elongation measurements were carried out on specimens prepared from cast and heat treated 7075 alloys containing Be and/or Zr. Different aging treatment were c...