Titanium and titanium alloy materials are commonly used in joint replacements, due to the high strength of the materials. Pathogenic microorganisms can easily adhere to the surface of the metal implant, leading to an increased potential for implant failure. The surface of a titanium-aluminum-vanadium (Ti-6Al-4V) metal oxide implant material was functionalized to deliver an small antibacterial m...

Ti–6Al–4V foams are produced by the expansion of pressurized argon pores trapped in billets created by powder metallurgy. Pore expansion during thermal cycling (840–1030 C, which induces transformation superplasticity in Ti–6Al–4V) improves both the foaming rate (by reducing the flow stress) and the final porosity (by delaying fracture of the pores and subsequent escape of the gas), as compared...

The purpose of this study was to characterize the etching mechanism, namely, the etching rate and the activation energy, of a titanium dental implant in concentrated acid and to construct the relation between the activation energy and the nanoscale surface topographies. A commercially-pure titanium (CP Ti) and Ti-6Al-4V ELI surface were tested by shot blasting (pressure, grain size, blasting di...

STATEMENT OF PROBLEM Information is lacking about the fatigue resistance of computer-aided design and computer-aided manufacturing (CAD-CAM) tooth-colored implant custom abutment materials. PURPOSE The purpose of this in vitro study was to investigate the reliability of different types of CAD-CAM tooth-colored implant custom abutments. MATERIAL AND METHODS Zirconia (Lava Plus), lithium disi...

Titanium alloys are extensively used in various fields of engineering, medicine, aerospace, marine due to its excellent mechanical properties. Its usage is more pronounced today in the field of biomedical implants due to its superior biocompatibility, corrosive resistance and high strength to weight ratio. It has poor abrasive wear resistance due to high coefficient of friction and low thermal ...

The success of any implant, dental or orthopaedic, is driven by the interaction of implant material with the surrounding tissue. In this context, the nature of the implant surface plays a direct role in determining the long term stability as physico-chemical properties of the surface affect cellular attachment, expression of proteins, and finally osseointegration. Thus to enhance the degree of ...

Three different implants, bare Ti-6Al-4V alloy, Ti-6Al-4V alloy coated with plasma-sprayed hydroxyapatite (PSHA), and Ti-6Al-4V alloy coated with electrochemically deposited hydroxyapatite (EDHA), were implanted into canine trabecular bone for 6 h, 7, and 14 days, respectively. Environmental scanning electron microscopy study showed that PSHA coatings had higher bone apposition ratios than thos...

Total knee replacement implants consisting of a Co-29Cr-6Mo alloy femoral component and a Ti-6Al-4V tibial component are the basis for the additive manufacturing of novel solid, mesh, and foam monoliths using electron beam melting (EBM). Ti-6Al-4V solid prototype microstructures were primarily α-phase acicular platelets while the mesh and foam structures were characterized by α(')-martensite wi...

OBJECTIVES To evaluate the reliability and failure modes of regular and horizontal mismatched platforms for implant-abutment connection varying the implant diameter. MATERIAL AND METHODS Regular (REG, n = 21, 4.0-mm-diameter implant) and horizontal mismatched (HM, n = 21, 4.6-mm-diameter implant) platform Ti-6Al-4V implants were restored with proprietary identical Ti-6Al-4V abutments and meta...

STATEMENT OF PROBLEM The success of titanium implants is due to osseointegration or the direct contact of the implant surface and bone without a fibrous connective tissue interface. PURPOSE The purpose of this study was to evaluate the osteoblast precursor response to titanium - 10 tantalum - 10 niobium (Ti-Ta-Nb) alloy and its sputtered coating. MATERIAL AND METHODS Ti-Ta-Nb coatings were ...