E. Olejnik, A. Janas, B. Grabowska, M. Kawalec, AGH University of Science and Technology, Faculty of Foundry Engineering, Krakow, Poland Casting technology was applied and research was carried out on two alloys based on the Ni3Al phase with variable carbon content of 0,2 and 1,25 wt. % C, respectively. Resistance to abrasive wear, friction coeffi cient and Vickers microhardness were determined....

Two-step thermal oxidation was proposed for Ti and Ti alloys as a surface-treatment process for preparing an anatase-containing TiO2 layer. This process consisted of treatment in a CO-containing atmosphere (first step) and subsequent treatment in air (second step). In this chapter, first, the current status of TiO2 coating onto Ti and Ti alloys for biomedical applications is reviewed; then our ...

Equiatomic FeMn alloys with varying Ag content (1–5 wt%) and hierarchical porosity show low ferromagnetic response during biodegradation reduction in the total biofilm biomass upon interaction S. aureus for 5 wt% containing materials.

2014 Measurements of magnetic susceptibility and spontaneous magnetization on face centred cubic platinum-iron alloys having compositions around Pt3Fe and also on alloys with lower iron contents, are reported. In the Pt3Fe superlattice region the alloys appear to be antiferromagnetic when ordered and ferromagnetic when disordered. The more dilute alloys are ferromagnetic, even down to 2 at. % o...

Internal attack of chromium containing alloys in mixed oxygen-chlorine environments occurs by the formation of pores which penetrate down grain boundaries of the alloys. No internal attack was detected in a binary Fe-20 %Cr alloy at 1200 K in environments containing 2500 ppm C12. The rate of internal attack of alloy 800H in such environments was increased by replacing the O2 in the gas by C02 ....

The oxidation and porcelain fusion characteristics of noble alloys containing a variety of minor oxidizable elements, including Cu, Sn, In, Ga, Mn, and Fe were investigated. Four porcelain alloys systems: a Pd-base alloy (Naturelle}, two Pd-Ag-based alloys (Jelstar and Acclaim}, and a high Au-alloy (SMG-3) were examined by scanning electron microscopy and energy dispersive spectroscopy after be...

Cobalt-Chromium (Co-Cr) alloys are classified as predominantly base-metal alloys and are widely known for their biomedical applications in the orthopedic and dental fields. In dentistry, Co-Cr alloys are commonly used for the fabrication of metallic frameworks of removable partial dentures and recently have been used as metallic substructures for the fabrication of porcelain-fused-to-metal rest...

Palladium-copper alloys continue to be of interest for hydrogen membrane applications because of their high catalytic activity for hydrogen dissociation, high hydrogen permeability, robustness, and degradation resistance in the presence of sulfur-containing compounds. This sulfur tolerance makes these alloys attractive for membrane applications where sulfur compounds are likely to be present, s...

Magnesium-rare earth based alloys are increasingly being investigated due to the formation of highly stable strengthening phases, activation of additional deformation modes and improvement in mechanical properties. Several investigations have been done to study the effect of rare earths when they are alloyed to pure magnesium and other Mg alloys. In this review, the mechanical properties of the...

It is well known that the properties of shape memory alloys, such as binary Ni-Ti (nitinol), are very sensitive to composition.[1-3] Especially on the Ni-rich side of stoichiometry, the martensite/austenite phase transformation temperature decreases abruptly when Ni is increased only a few tenths of a weight percent.[4] In ternary high temperature shape memory alloys (HTSMAs) containing Pt, Pd,...