The fracture behaviour of human cortical bone was analysed considering a miniaturized version of the Double Cantilever Beam (DCB) test. A specific data reduction scheme based on crack equivalent concept was used to obtain the resistance curves. The definition of the cohesive laws mimicking the fracture process was performed measuring the crack tip opening displacement by digital image correlati...

Structural materials used for safety critical applications require high strength and simultaneously high resistance against crack growth, referred to as damage tolerance. However, the two properties typically exclude each other and research efforts towards ever stronger materials are hampered by drastic loss of fracture resistance. Therefore, future development of novel ultra-strong bulk materi...

Bulk-metallic glasses (BMGs) are now candidate materials for structural applications due to their exceptional strength and toughness. However, their fatigue resistance can be poor and inconsistent, severely limiting their potential as reliable structural materials. As fatigue limits are invariably governed by the local arrest of microscopically small cracks at microstructural features, the lack...

In this paper, the thermo-mechanical reliability of Cu/ultra low-k interconnects under chip to package interaction was investigated using finite element modeling and modified edge liftoff test (MELT). The crack propagation behavior in the low-k interconnect was simulated based on the crack tip opening displacement method (CTOD) and the maximum hoop stress criterion. In a six-level Cu/low-k inte...

In vivo, bone cement is subject to cyclic loading in a fluid environment. However, little is known about the effect of moisture absorption on the fatigue crack propagation resistance of bone cement. The effect of moisture absorption at 37 degrees C on the fatigue crack propagation resistance of a common bone cement (Endurance, DePuy, Orthopaedics, Inc.) was examined. Preliminary fracture toughn...

While a new tire may have excellent resistance to crack initiation and propagation between the steel belts, an aged tire of the exact same construction can exhibit dramatically reduced crack growth resistance, which in some cases may contribute to tire failure. This article will review the research that has gone into quantifying the rate of oxidation the steel belt rubber oxidizes in different ...

Ambientto elevated-temperature fracture and fatigue-crack growth results are presented for five MoMo3Si-Mo5SiB2–containing -Mo matrix (17 to 49 vol pct) alloys, which are compared to results for intermetallic-matrix alloys with similar compositions. By increasing the -Mo volume fraction, ductility, or microstructural coarseness, or by using a continuous -Mo matrix, it was found that improved fr...

The present paper explores quasi-cleavage processes driven by dislocation pileups against a Dislocation Free Zone (DFZ). The nanoscopic growth of the main crack consists of sequences of nanocrack formation in DFZ and its subsequent linkage with the main crack. Under mode I loading, the equilibrium locations of individual dislocations and the equilibrium number of dislocations are determined by ...

It is well known that the mechanical properties of materials depend of the rolling direction, which means that the direction of specimen cutting affect the obtained values. This feature also exists in the welded joint, where the anisotropy is caused by direction of the deposit welded layers. One high-carbon steel is surface welded by flux-cored wire and specimens were cut in order to determine ...

This paper is concerned with some aspects of nonuniform stressing above a deep creeping portion of a fault zone prior to a large crust-breaking earthquake. The model that we use involves a slipping crack, representing the deeper, more stably sliding portions of the fault zone, which penetrates upward from depth and is blocked in the lower region of the seismogenic zone. When conditions are unif...