In this work, the mode I fracture toughness of dissimilar metal-composite adhesive joints is experimentally investigated using double cantilever beam (DCB) test. The particular joint under study resulted by joining a thin titanium sheet with carbon fiber reinforced plastic (CFRP) laminate and envisioned to be implemented in hybrid laminar flow control system future aircraft. Four different indu...

The crack growth resistance of human dentin was characterized as a function of relative distance from the DEJ and the corresponding microstructure. Compact tension specimens were prepared from the coronal dentin of caries-free 3rd molars. The specimens were sectioned from either the outer, middle or inner dentin. Stable crack extension was achieved under Mode I quasi-static loading, with the cr...

This paper characterizes the fracture toughness of layer-by-layer (LBL) manufactured thin films with elastic polyurethane, a tough polymer, and poly(acrylic acid) as a stiffening agent. A single-edge-notch tension (SENT) specimen is used to study mode I crack propagation as a function of applied loading. Experimental results for the full-field time histories of the strain maps in the fracturing...

Relationships between crack initiation and crack growth toughness are reviewed by examining the crack tip fields and microscopic (local) and macroscopic (continuum) fracture criteria for the onset and continued quasi-static extension of cracks in ductile materials. By comparison of the micromechanisms of crack initiation via transgranular cleavage and crack initiation and subsequent growth via ...

the cracked brazilian disc (cbd) specimen is widely used in order to determine mode-i/ii and mixed-mode fracture toughness of a rock medium. in this study, the stress intensity factor (sif) on the crack-tip in this specimen is calculated for various geometrical crack conditions using the extended-finite element method (x-fem). this method is based upon the finite element method (fem). in this m...

Mechanisms influencing the plane-strain fracture toughness behavior of commercial aluminum-lithium alloys at cryogenic temperatures are investigated as a function of microstructure and plate orientation. It is confirmed that certain alloys show a marked increase in tensile ductility and toughness with decrease in temperature, although such behavior is not found in the short-transverse orientati...

Ceramic coatings deposited on metal substrates generally develop significant compressive stresses when cooled from the temperature at which they are processed as a result of thermal expansion mismatch. One of the main failure modes for these coatings is edge delamination. For an ideally brittle interface, the edge delamination of a compressed thin film involves mode II interface cracking. The c...

In this paper, effects of ply orientation of adjacent plies with (ϕ//θ) interfaces on mode II critical strain energy release rate (fracture toughness) of multidirectional (MD) laminate has been studied. Ply orientation of adjacent plies is one of the most important parameters affects the mode II critical strain energy release rate () in the initiation of the delamination. To  study this paramet...