Deformation behavior and microstructure evolution of NiTiCu shape memory alloy (SMA), which possesses martensite phase at room temperature, were investigated based on a uniaxial compression test at the temperatures of 700~1000 ◦C and at the strain rates of 0.0005~0.5 s−1. The constitutive equation of NiTiCu SMA was established in order to describe the flow characteristic of NiTiCu SMA, which is...

The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...

The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...

Calculations verify that carbon diffusion may occur during the lath martensite fomtion. Accordingly,the diffusion of int2rstitial ator ions must be taka into account nhfn martmitic transformtion is defined as a diffusionless transformation. In derivation of the kinetics equation of the ath& martensitic transfomtion,rzgardng the c a r h diffusion, i .e.the enrichment of the austenite during the ...

Following the mathematical approach of Kelly (2003), rigorous version of infinitesimal deformation approach (ID) was applied to analyze fcc  bcc martensitic phase transformation observed in Fe-31wt Ni alloys considering the twinning shear system as the lattice invariant system (LIS). The expressions for crystallographical parameters associated with the martensitic phase transformation such as...

this study was conducted in order to investigate the influence of plastic deformation on the transformation of retained austenite in a trip steel with a high content of al and a low content of si. to the aim, appropriate treatments were used to produce the starting material (trip steel). the microstructure of the obtained steel was composed of bainite and phases including ferrite and retained a...

Annealing process is critical to mechanical properties and microstructure of DP steel. For steel with strength grade 590MPa, experiments different combinations intercritical annealing temperature over-aging were carried out during annealing. The tensile tests the final products nanohardness phases made, microstructures analyzed. results indicated that higher was favorable volume fraction marten...

This study was conducted in order to investigate the influence of plastic deformation on the transformation of retained austenite in a TRIP steel with a high content of Al and a low content of Si. To the aim, appropriate treatments were used to produce the starting material (TRIP steel). The microstructure of the obtained steel was composed of bainite and phases including ferrite and retained a...