The new superaustenitic stainless steel UNS S32654 (Avesta Sheffield 654 SMO) is proposed for condenser tubes in desalination and power plants. A number of tests illustrating its corrosion resistance in a variety of chloride containing environments are being reviewed in terms of pitting, crevice corrosion and stress corrosion cracking. Relevant mechanical and physical properties are described. ...

Concrete is usually highly alkaline (pH around 12), thus protecting reinforcement against corrosion. The occurrence of oxides is favored when the medium pH surrounding the bar is in values near to 9 or lower. Aggressive substances for reinforcements generally enter concrete through its pore structure, and cracks tend to decrease pH, stimulating corrosion process. There are several causes for cr...

In this paper, an experimental study is presented on the influence of PET warping on shear performance, such as diagonal shear cracking load, peak load, and energy dissipation of RC columns with stirrup corrosion before strengthening. The experimental program involved an electrochemical process to accelerate the migration of chlorides from an external electrolyte into the tested columns, a wett...

The causes and the prevention of carbon steel corrosion in amine systems are reviewed. The corrosive agents are acid gases, oxygen, heat stable salts, amine degradation products, and, in refineries, gas contaminants such as ammonia and hydrogen cyanide. Corrosion mechanisms are provided for carbon steel exposed to amine solutions and for amine regenerator overhead systems containing aqueous con...

Cost functions, associated with the gamma process for modelling deterioration, are extended to include multiple failure modes. The application of these cost functions is demonstrated by an example in the process industry. We consider an elbow in a pipeline, which is susceptible to thinning due to corrosion and stress corrosion cracking. The optimal inspection interval and replacement levels are...

Unusually rapid closure of stressed fractures, observed in the initial stages of loading and at low temperatures, is examined using models for subcritical crack growth and pressure solution. The model for stress corrosion examines tensile stress concentrations induced at the Hertzian contact of propping fracture asperities, and mediates fracture growth according to a kinetic rate law. Conversel...

Corrosion is a natural process that seeks to reduce the binding energy in metals. The end result of corrosion involves a metal atom being oxidized. Surface corrosion on aluminum aircraft skins, near joints and around fasteners, is often an indicator of buried structural corrosion and cracking In this paper we proposed a new method on which we are moving towards designing a method to detect the ...

In this work, Slow Strain Rate Test (SSRT) testing, Light Optical Microscopy (LOM) and Scanning Electron Microscopy (SEM) were used to study the effect of microstructure, corrosive environments and cathodic polarisation on stress corrosion cracking (SCC) of two grades of high strength steels, Type A and Type B. Type A is manufactured by quench and tempered (Q&T) method. Type B, a normalize stee...

The effect of hydrogen on the corrosion and stress corrosion cracking of the magnesium AZ91 alloy has been investigated in aqueous solutions. Hydrogen produced by corrosion in water diffuses into, and reacts with the Mg matrix to form hydride. Some of the hydrogen accumulates at hydride/Mg matrix (or secondary phase) interfaces as a consequence of slow hydride formation and the incompatibility ...

Cracking of the concrete cover due to corrosion is defined as the serviceability limit state of reinforced concrete structures. This study evaluated the influence of a mineral admixture i.e. nano wollastonite on corrosion performance and serviceability of reinforced concrete structures by performing an accelerated corrosion test on ten reinforced concrete beams under a sustained load. To do so,...