The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...

The basic problem of main pipelines non-destructive examination is reliability and validity of obtained parameters of flaws (including stress-corrosion cracks). One of the most rapid and efficient NDT techniques for main pipelines is the method of magnetic flux leak (MFL) over defect. In accordance with magnetic method canon the examination reliability (that is probability of crack detection st...

Pitting corrosion is one of the most common forms of localized corrosion. Corrosion pit results in a stress concentration and fatigue cracks usually initiate and propagate from these corrosion pits. Aging structures may fracture when the fatigue crack reaches a critical size. This paper experimentally simulates the effects of pitting morphologies on the static and fatigue behavior of steel bars...

The creep aging behaviors of retrogressed Al-Zn-Mg-Cu alloy were studied by uniaxial tensile creep tests at 140 ◦C. The effects of creep aging time and applied stress on microstructures and properties of the studied alloy were investigated by using transmission electron microscope (TEM), hardness, and corrosion resistance tests. Results show that the effects of the creep aging process on micros...

The main drawback of a conventional stenting procedure is the high risk of restenosis. The idea of a stent that "disappears" after having fulfilled its mission is very intriguing and fascinating, since it can be expected that the stent mass decreases in time to allow the gradual transmission of the mechanical load to the surrounding tissues owing to controlled dissolution by corrosion. Magnesiu...

The effect of static and cyclic loading conditions on the stress corrosion cracking of unidirectional glass reinforced polymer (GRP) rods used in composite high voltage insulator has been investigated. A series of stress corrosion experiments have been performed on unidirectional E-glass/modified polyester composite rods. The rods have been subjected to mechanical tensile static and cyclic stre...

This paper describes the non-uniform corrosion characteristics and mechanical properties of reinforcement under coupled action of carbonation and static loading. The two parameters, namely area-box (AB) value and arithmetical mean deviation (Ra), are adopted to characterize the corrosion morphology and pitting distribution from experimental observations. The results show that the static loading...

A review is provided about the current research on magnesium/magnesium alloys corrosion in the industry. Except for reviewing the kinds of corrosion on galvanic corrosion, stress corrosion, and corrosion fatigue, its corresponding mechanisms are also explained, such as the influence of metallurgical factors, and environmental factors. Furthermore, the protection of magnesium/magnesium alloys co...

A modelling effort was made to try to predict the life of downhole tubes or casings, synthetically considering the effect of service influencing factors on corrosion rate. Based on the discussed corrosion mechanism and corrosion processes of downhole tubes, a mathematic model was established. For downhole tubes, the influencing factors are environmental parameters and stress, which vary with se...

stress-corrosion cracking (scc) tests were conducted in the near-neutral ph standard solution, ns4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...