Abstract An Al-5Mg alloy (AA5083) block, deposited over an AA6061 substrate by wire-arc additive manufacturing, was electrochemically tested along two different cross-sectional planes cyclic polarization in 3.5 wt.% NaCl. The layers and the interlayer boundaries showed similar behavior regardless of direction. corrosion both mainly attributed to presence relatively coarse intermetallic Al(Fe, M...

A comprehensive kinetic analysis was established to investigate the electromigration (EM) enhanced intermetallic compound (IMC) growth and void formation for Sn-based Pb-free solder joints with Cu under bump metallization (UBM). The kinetic model takes into account Cu–Sn interdiffusion and current stressing. Derivation of the diffusion coefficients and the effective charge numbers for the inter...

Laves-phase Nb(1+c)Fe(2-c) is a rare itinerant intermetallic compound exhibiting magnetic quantum criticality at c(cr)∼1.5%Nb excess; its origin, and how alloying mediates it, remains an enigma. For NbFe(2), we show that an unconventional band critical point above the Fermi level E(F) explains most observations and that chemical alloying mediates access to this unconventional band critical poin...

The growth kinetics of intermetallic compound layers formed between eutectic Sn–58Bi solder and (Cu, electroless Ni–P/Cu) substrate were investigated at temperature between 70 and 120◦C for 1 to 60 days. The layer growth of intermetallic compound in the couple of the Sn–58Bi/Cu and Sn–58Bi/electroless Ni–P system satisfied the parabolic law at given temperature range. As a whole, because the va...

The formation of microporosity in modified Al-Si alloys has been reviewed in the present study. A major concern in modification is the increased tendency to form microporosity in the macro-shrinkage free Al-Si alloy castings. It has also been demonstrated that at low hydrogen contents (0.1cc/ 100g, Al), where only shrinkage porosity should occur, the effect of Sr-modification on porosity conten...

This multi-layer program has examined the oxidation resistance of Al-rich coatings made by chemical vapor deposition and pack cementation on ferritic-martensitic (e.g. T91, Fe-9Cr-1Mo) and austenitic (Type 304L, Fe-18Cr-8Ni) substrates at 650°-800°C. The main goal of this work was to demonstrate the potential benefits and problems with alumina-forming coatings. To evaluate their performance, ox...