La1-xSrxAlO3 (x=0 to 0.4) perovskite materials were synthesized by the reverse strike co-precipitation method and their soot oxidation activity was evaluated. All the catalysts synthesized were characterized using XRD, BET specific surface area, FESEM and XPS techniques. As analyzed by XRD, La1-xSrxAlO3 <...

Sol-gel derived sulfur modified and pure ZnO nanorod were prepared using zinc chloride and thiocarbamide as raw materials. Prepared nanorods were characterized by means of X-ray diffraction (XRD), thermogravimetry- differential scanning calorimetry (TG–DSC), UV- Vis absorption spectroscopy, Brunauer Emmett Teller (BET) specific surface area and Barrett Joyner Halenda (BJH) pore size distributio...

S-doped and bare mesoporous TiO2 were prepared using titanium tetraisopropoxide and thiocarbamide as raw materials. Prepared materials were characterized by means of fourier transform infrared spectroscopy FT-IR, thermogravimetry-differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), UV–Vis absorption spectroscopy, Brunauer–Emmett–Teller (BET) specific surface area and Barrett–Joy...

Sol-gel derived sulfur modified and pure ZnO nanorod were prepared using zinc chloride and thiocarbamide as raw materials. Prepared nanorods were characterized by means of X-ray diffraction (XRD), thermogravimetry- differential scanning calorimetry (TG–DSC), UV- Vis absorption spectroscopy, Brunauer Emmett Teller (BET) specific surface area and Barrett Joyner Halenda (BJH) pore size distributio...

Pure Anatase Titania (TiO2), mixed 1.0 wt.% Cerium-Anatase Titania (1.0 wt.%CeO2-TiO2), and mixed 1.0 wt.% Zirconia-Anatase Titania (1.0 wt.%ZrO2-TiO2) nano powders were synthesized by co-precipitation method and characterized using X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area analysis, UV-Vis diffuse reflectance spect...

Metal doped TiO2 catalysts were synthesized by sol-gel method and their activities were determined for degradation of methyl orang as a pollutant. Nd-doped TiO2 showed the maximum activity comparing with others. Colloidal SiO2 was used as a support to increase the surface area and also the activity. Nano-TiO2/SiO2/Nd was synthesized by sol-gel method and it was characterized using XRD, XRF, SEM...

In this research iron manganese oxide nanocomposites were prepared by co-precipitation, sol-gel and mechanochemical methods by using iron (III) nitrate, iron (II) sulfate and manganese (II) nitrate as starting materials. These nanocomposites were prepared in the presence of various catalyst beds. The polyvinyl pyrrolidon (PVP) was used as a capping agent to control the agglomeration of the nano...

Nanocrystalline strontium hexaferrite (SrFe12O19) powders have been successfully synthesized using the facile Co-precipitation method. The ferrite precursors were achieved from mixtures of strontium and ferric chloride in an aqueous medium without any surfactant and soft template. The as-received powders were calcined at 800 and 1000 ˚C for 2 hours in air. The final powders were characterized b...

Carbon molecular sieves were prepared from petroleum coke by chemical activation. The effects of activation temperature, holding time, preliminary treatments and activated agent ratio on surface area, pore structure of the carbon molecular sieves produced in our lab were investigated. The specific surface area and average pore size of the carbon are obviously increased with increasing use of ac...

This paper examines the surface-related capacitance C/S of carbons with average micropore widths between 0.73 and 1.80 nm, using 1-2M H2SO4, 6M KOH and 1M (C2H5)4NBF4 in acetonitrile as electrolytes. Following corrections for pseudocapacitance effects for the aqueous electrolytes and the use of an average surface area suggested by independent techniques, different from the BET area, it appears ...