The present study investigated the effect of grinding on roughness, flexural strength, and reliability of a zirconia ceramic before and after heat treatment. Seven groups were tested (n = 15): a control group (labeled CG, untreated), and six groups of samples ground with diamond discs, simulating diamond burs, with grits of 200 µm (G80); 160 µm (G120), and 25 µm (G600), either untreated or heat...

Yttria stabilized zirconia (3 mol% YSZ) ceramics were prepared by Flash-SPS, while allowing high heating rates up to 200 °C/s, which led the extremely fast densification within a few seconds. The had strong impact on sintering mechanisms, in terms of and grain growth. While specimens ended with 5–15 vol% porosity limited growth (< 350 nm), their hardness is higher than fully dense counterpart S...

In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural strength of the non-layered specimens was 1,220 MPa for dense zirconia and 220 to 30...

 This study aimed to investigate the impact of N-vinylcaprolactam (NVC) and Nano-sized yttria-stabilized zirconia (YSZ), separately and simultaneously, on the mechanical properties of the commercial glass ionomer cements (GICs). Methods: The NVC is able to ameliorate the mechanical and surface properties of glass ionomers; however, its effect hasn’t been investigated in conjunc...

Multilayer thermal barrier coatings (TBCs) on superalloy substrates are comprised of an intermetallic bond coat, a thermally grown oxide (TGO) layer, and a porous zirconia top coat that provides thermal protection. The TGO attains a thickness of 1±10 lm prior to failure, while the bond coat and zirconia layer are each about 50±100 lm thick. The preferred method for manufacturing TBCs comprises ...

Objective: The aim of the study was to make an inventory of current literature on the bond strength between zirconia and veneering porcelain after surface treatment of zirconia by grinding with diamond bur and/or with airborne-particle abrasion. Material and methods: The literature search for the present review was made following recommended guidelines using acknowledged methodology on how to d...

in this study the effect of nano meter size zro2 particles on the microstructure, densification and hydration resistance of magnesite –dolomite refractories was investigated. 0, 2, 4, 6 and 8 wt. % zro2 particles that were added to magnesite –dolomite refractories containing 35 wt. % cao. the hydration resistance was measured by change in the weight of specimens after 72 h at 25℃ and 95% relati...

Determination of nano particle size is substantial since the nano particle size exerts a significant effect on various properties of nano materials. Accordingly, proposing non-destructive, accurate and rapid techniques for this aim is of high interest. There are some conventional techniques to investigate the morphology and grain size of nano particles such as scanning electron microscopy (SEM)...

in this research, the effect of different biopolymers such as polyethylene glycol (peg) and polyvinylalcohol (pva) on synthesis and characterization of polymer/cobalt ferrite (cf) nano-composites bymechanical alloying method has been systematically investigated. the structural, morphological andmagnetic properties changes during mechanical milling were investigated by x-ray diffraction (xrd),fo...

Thermal decomposition of Zr(C(2)O(4))(2)·4H(2)O within an autoclave or in a conventional tube furnace at temperatures below 380 °C resulted in nano- and micron-sized ZrO(2), respectively. Reactions under autogenic pressure yielded monodisperse monoclinic (m) and tetragonal (t) ZrO(2) nanoparticles with an average diameter of ~8 nm and interconnected t-ZrO(2) nanoparticles with diameters of ~4 n...