M. Ghamari

[ 1 ] - COMPOSITION DEPENDENCE OF SPECTROSCOPIC PROPERTIES AND TRANSPARENCY OF SiO2-TiO2-Na2O GLASS IN 200-1100 nm

Abstract: Glassy samples with xTiO2 .3SiO2 .Na2O composition that (8≤x≤40) (molar) were casted in refractory steel molds after melting at air as parallel palates. After polishing and getting to desire thickness, UV-VIS spectrometry in 200 -1100 nm was measured on samples. Glass density was measured by a sensitive micro balance and was found that by increasing titanium dioxide of glasses, glass ...