COMPOSITION DEPENDENCE OF SPECTROSCOPIC PROPERTIES AND TRANSPARENCY OF SiO2-TiO2-Na2O GLASS IN 200-1100 nm

نویسندگان

  • B. Mirhadi
چکیده مقاله:

Abstract: Glassy samples with xTiO2 .3SiO2 .Na2O composition that (8≤x≤40) (molar) were casted in refractory steel molds after melting at air as parallel palates. After polishing and getting to desire thickness, UV-VIS spectrometry in 200 -1100 nm was measured on samples. Glass density was measured by a sensitive micro balance and was found that by increasing titanium dioxide of glasses, glass density increases. Results from UV-VIS spectroscopy show that increase of titanium dioxide decreases light transmission and this value reaches zero for sample with 40 molar percent of titanium dioxide. One reason of this reduction is formation of crystalline phase in glass, in which, by increasing titanium content crystalline phase will be increased, results of X-ray diffraction and electron microscopy confirm this claim.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

some properties of fuzzy hilbert spaces and norm of operators

in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...

15 صفحه اول

PREPARATION OF Fe/GLASS COMPOSITE BY REDUCTION OF Na2O– Fe2O3–B2O3–SiO2–ZnO GLASS AND GLASS CERAMICS

In the present study, the feasibility of α-Fe ferromagnetic phase formation in glass and glass-ceramic by reduction in hydrogen atmosphere have been investigated. The glass with the composition of 35Na 2 O–24Fe2O3–20B 2O3 – 20SiO 2 –1ZnO (mol %) was melted and quenched by using a twin roller technique. As quenched glass flakes were heat treated in the range of 400-675 °C for 1-2 h in h...

متن کامل

Magnetic properties of praseodymium ions in Na2O–Pr2O3–SiO2 glasses

Sodium praseodymium silicate glasses of nominal composition 0.3Na2O xPr2O3 (0.7 x)SiO2, where 0pxp0:10; have been studied by magnetisation and X-ray photoelectron spectroscopy (XPS). The magnetisation data fail to collapse to a single curve in the M versus H=T representation for all values of x and the spread increases with x; indicating an increase in the magnetic exchange interaction. The M v...

متن کامل

EFFECT OF TiO2 ADDITION ON BONDING STRENGTH OF CaO-P2O5 Na2O-TiO2 BIOACTIVE GLASS CERAMIC COATING

The effect of titanium dioxide addition on bonding strength of CaO-P2O5 -Na 2O-TiO2glass-ceramic system was investigated as a coating on titanium substrate. Thus, different amounts of TiO2 (2, 3.5 and 5mol %) were added to the base glass batch composition. The prepared glaze slips were applied on the substrate by dip coating method, dried and then heat treated at various temperatures. After tha...

متن کامل

Dependence of Photocatalytic Activity of TiO2-SiO2 Nanopowders

Structural properties and chemical composition change the photocatalytic activity in TiO2-SiO2 nanopowder composite. The SiO2-TiO2 nanostructure is synthesized based on sol–gel method. The nanoparticles are characterized by x-ray fluorescents (XRF), x- ray diffraction (XRD), tunneling electron microscopy (TEM), field emission scanning electron microscopy (FE-SEM), UV-vis. Spectrophotometer and ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 9  شماره 2

صفحات  36- 40

تاریخ انتشار 2012-06

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023