Ehsan Taheri Nassaj
Department of Material Science Engineering, Tarbiat Modares University, Tehran, Iran.
[ 1 ] - Corrosion Properties of 70SiO2-15TiO2-15ZrO2 Ceramic Membrane
The 70SiO2-15TiO2-15ZrO2 membrane was prepared by a sol-gel procedure. The corrosion behavior of microporous toplayers along with the membrane characterization in terms of pore size, surface area, pore volume and weight loss is described. The final ceramic membrane with a thickness of 400 nm and uniform surface was obtained. This membrane confirmed the fine microporous characteristic with mean ...
[ 2 ] - Sol-gel synthesis and characterization of alumina-15%mullite composite nanopowder
Homogeneous distribution of mullite in the matrix of alumina can be obtained through sol-gel method. In this work, nanopowder of alumina-mullite composite was synthesized with high homogeneity and high purity. So aluminum chloride hexahydrate and tetraethyl orthosilicate were used instead of alumina or mullite nanopowder. Studying the simultaneouse thermal analysis (STA) of mullite precursor re...
[ 3 ] - SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN
A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic Separation and leaching with HCl and chemical bleaching treatment by using sodium dithionite (Na 2 S 2O4 ) as reducing agent in acidic media (H 2SO 4 ) were used. Pur...