Corrosion Properties of 70SiO2-15TiO2-15ZrO2 Ceramic Membrane
نویسندگان
چکیده مقاله:
The 70SiO2-15TiO2-15ZrO2 membrane was prepared by a sol-gel procedure. The corrosion behavior of microporous toplayers along with the membrane characterization in terms of pore size, surface area, pore volume and weight loss is described. The final ceramic membrane with a thickness of 400 nm and uniform surface was obtained. This membrane confirmed the fine microporous characteristic with mean pore size < 2 nm. After corrosion test, the corroded membrane revealed a surface with non-uniform coverage of the toplayer. The heated ceramic membrane after and before corrosion test was amorphous. Dissolution of ions was increased in acidic and basic solutions. The weight less of samples increased when pH increased at RT. Porosity of samples increased after the corrosion test. The pore size of membrane increased as compared to the pore size of the original membrane after corrosion conditions. Surface area of the membrane increased in basic solution whereas decreased in acidic solution.
منابع مشابه
control of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولFABRICATION AND CHARACTERIZATION OFHIGH PERFORMANCE CERAMIC MEMBRANE HAVINGNANOMETRE PORES
Abstract: In this study, carbon nanotubes (CNTs) were grown directly in the pores of micro porous pyrex membranesand consequently ceramic membranes with very fine pores and high porosity were achieved. Our experiment was donein two stages. Initially cobalt powder with different percent was homogeneously mixed with pyrex powder. In order toproduce row membranes, each of these mixtures were compa...
متن کاملsome properties of fuzzy hilbert spaces and norm of operators
in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...
15 صفحه اولSintering properties of zirconia-based ceramic composite
This study examines the effects of different ZrB2 content on various mechanical properties and electrical conductivity of ZrB2/Y-TZP composite. Composites with ZrB2 content of up to 20 wt-% were particularly beneficial at the lower sintering temperature range by achieving greater densification and better hardness than Y-TZP monolith. In contrast to the trends estimated from rule of mixture, the...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 2 شماره 3
صفحات 15- 26
تاریخ انتشار 2014-08-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023