The Role of Factors Influencing the Optical Properties of Yttrium Aluminum Garnet Ceramic Body
نویسنده
چکیده مقاله:
Yttrium Aluminum Garnet (Y3Al5O12) is a transparent ceramic with a wide range of applications such as high mechanical strength windows, high power laser sources and radiation detectors. The most important challenge in making these ceramics is the problem of low light transmittance, especially in the visible area in the range of 400 to 700 nm, which is greatly affected and reduced by various factors. So far, many efforts have been made to reduce the structural and microstructural defects of components made using this material to bring the optical properties of the material closer to theoretical values. In the present study, YAG transparent ceramics with high optical properties were fabricated by solid state synthesis method using Y2O3 and Al2O3 nanopowders and then Sintered under vacuum furnace at 1730°C during 12 hours And the combination of TEOS (tetraethyl orthosilicate) was used as sintering aid. Then bodies were annealed in two steps at 1200°C for 4 hours and about 1300°C for 5 hours. SEM, PL, EDX, UV-Vis characterization tests were used for microstructural and optical examination of ceramic bodies. The results showed that the structural and atomic defects as well as the presence of some impurities such as Ce+3 caused the absorption and reduction of light transmittance in the visible wavelength ranges. Studies have shown that the most important factor in reducing optical properties is the defects in structure that cause light scattering.
منابع مشابه
control of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولEffect of Synthesis Temperature on the Electrochemical Properties of Yttrium Aluminum Garnet
In this study, yttrium aluminum garnet (YAG) was prepared using a facile electrochemical technique. Four samples were synthesized in 0, 20, 40 and 60°C by electrochemical pulse deposition and were then calcined at 1200°C. The effect of synthesis temperature on morphology and structure of YAG was studied using X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron micro...
متن کاملthe analysis of the role of the speech acts theory in translating and dubbing hollywood films
از محوری ترین اثراتی که یک فیلم سینمایی ایجاد می کند دیالوگ هایی است که هنرپیش گان فیلم میگویند. به زعم یک فیلم ساز, یک شیوه متأثر نمودن مخاطب از اثر منظوره نیروی گفتارهای گوینده, مثل نیروی عاطفی, ترس آور, غم انگیز, هیجان انگیز و غیره, است. این مطالعه به بررسی این مسأله مبادرت کرده است که آیا نیروی فراگفتاری هنرپیش گان به مثابه ی اعمال گفتاری در پنج فیلم هالیوودی در نسخه های دوبله شده باز تولید...
15 صفحه اولfactor influencing the adoption of internet banking
دوره مشترک کارشناسی ارشد بازاریابی و تجارت الکترونیک دانشگاه تربیت مدرس_ دانشگاه تکنولوژی lule? چکیده پایان نامه عوامل موثر بر پذیرش اینترنت بانک توسط مشتریان پیشرفت فناوری اطلاعات و ارتباطات و به طور خاص رشد اینترنت جهت تراکنش های معاملات بازرگانی، تاثیر بسیار عمیقی در صنعت بانکداری داشته است.این در حالی ست که نفوذ بانکداری اینترنتی در کشورهای در حال توسعه بسیار کندتر از نفوذ آن ...
15 صفحه اولBulk optical damage thresholds for doped and undoped, crystalline and ceramic yttrium aluminum garnet.
We measured the bulk optical damage thresholds of pure and Nd-doped ceramic yttrium aluminum garnet (YAG), and of pure, Nd-doped, Cr-doped, and Yb-doped crystalline YAG. We used 9.9 ns, 1064 nm, single-longitudinal mode, TEM00 pulses, to determine that the breakdown thresholds are deterministic, with multiple-pulse thresholds ranging from 1.1 to 2.2 kJ/cm2.
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 8 شماره 3
صفحات 29- 40
تاریخ انتشار 2019-12
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023