Stress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments

نویسندگان

  • B. Fang Environmental Corrosion Center, Institute of Metal Research Chinese Academy of Science, Shenyang, P. R. China, 10016 and CANMET Materials Technology Laboratory 568 Booth Street, Ottawa, Ontario, Canada K1A 0G1
  • E-H. Han Environmental Corrosion Center, Institute of Metal Research Chinese Academy of Sciences, Shenyang, P. R. China, 10016
  • J. Li CANMET Materials Technology Laboratory 568 Booth Street, Ottawa, Ontario, Canada K1A 0G1
  • M. Elboujdaini Environmental Corrosion Center, Institute of Metal Research Chinese Academy of Sciences, Shenyang, P. R. China, 10016
  • R. Revie CANMET Materials Technology Laboratory 568 Booth Street, Ottawa, Ontario, Canada K1A 0G1
  • W. Zheng CANMET Materials Technology Laboratory 568 Booth Street, Ottawa, Ontario, Canada K1A 0G1
چکیده مقاله:

Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen tested in soil purged with 5% CO2 +95%N2 than in the specimen tested in NS4 solution purged with the same gas. These observations show that samples in soil solution are more susceptible to pitting than those in NS4 solution. When the pit reached a critical size, the increased stress concentration around the pits, resulted in transition to a crack.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

stress- corrosion crack initiation of high-strength pipeline steel in near-neutral ph environments

stress-corrosion cracking (scc) tests were conducted in the near-neutral ph standard solution, ns4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...

متن کامل

Stress Corrosion Crack Growth Mechanism on SUS316L Stainless Steel

The stress corrosion cracking (SCC) of stainless steel is one of the biggest problems for maintaining atomic power and chemical plants. However the mechanism has not been solved because of difficulty in observing hydrogen movement. In order to solve this problem, the author has developed a new SCC test method that enables the super Kelvin force microscope (SKFM) and the Kelvin force microscope ...

متن کامل

An Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade

First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...

متن کامل

Observations on the Stress-corrosion Crack Propagation Characteristics of High-strength Steels

The relationahip between streas-corroslon crftck velocity and cracktip stress intensity is discussed. In most high-strength steels there is a wide range of stress intensity over which crack velocity is essentially constant. Methods of estimating this velocity are described. Values for a variety of high-strength steels are presented and the effects of metallurgical variables are indicated. Impli...

متن کامل

An Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution

The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...

متن کامل

Iron metabolism in anoxic environments at near neutral pH.

Anaerobic dissimilatory ferric iron-reducing and ferrous iron-oxidizing bacteria gain energy through reduction or oxidation of iron minerals and presumably play an important role in catalyzing iron transformations in anoxic environments. Numerous ferric iron-reducing bacteria have been isolated from a great diversity of anoxic environments, including sediments, soils, deep terrestrial subsurfac...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 3  شماره 1

صفحات  20- 25

تاریخ انتشار 2006-06-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023