Sliding Wear Behaviour of Walnut Shell Powder Filled Vinyl Ester/ WSP Green Composites
نویسندگان
چکیده مقاله:
Polyvinyl ester green composites were synthesized with walnut shell powder (WSP) by in-situ polymerization technique. The green composites have been evaluated for mechanical properties such as tensile strength, tensile modulus and hardness. Sliding wear loss, specific wear rate and coefficient of friction were investigated by using computerized pin-on–disc machine at normal applied loads of 20, 30 and 40N; at a sliding velocity of 1.5 m/s and at two abrading distances viz., 100 and 200 m. The results indicate that the wear volume loss increases with increasing abrading distance/load. It was found that WSP filled vinyl ester composites exhibit lower wear rate and higher coefficient of friction as compared to vinyl ester green composites. Further, the worn surfaces were examined by scanning electron microscopy (SEM), to give insight in to the wear mechanism, while their mechanical properties were investigated using tensile strength, tensile modulus and hardness test machines.
منابع مشابه
sliding wear behaviour of walnut shell powder filled vinyl ester/ wsp green composites
polyvinyl ester green composites were synthesized with walnut shell powder (wsp) by in-situ polymerization technique. the green composites have been evaluated for mechanical properties such as tensile strength, tensile modulus and hardness. sliding wear loss, specific wear rate and coefficient of friction were investigated by using computerized pin-on–disc machine at normal applied loads of 20,...
متن کاملMetal Powder-filled Polyethylene Composites. v. Thermal Properties Metal Powder-filled Polyethylene Composites. v. Thermal Properties
Thermal properties—such as thermal conductivity, thermal diffusivity, and specific heat—of metal (copper, zinc, iron, and bronze) powder-filled high-density polyethylene composites are investigated experimentally in the range of filler content 0–24% by volume. Experimental results show a region of low particle content, 0–16% by volume, where the particles are distributed homogeneously in the po...
متن کاملExperimental Study on Wear Behaviour of Sic Filled Hybrid Composites Using Taguchi Method
The popularity of composite materials usage is increasing due to its superior strength characters racing the traditional materials in strength to weight ratio. The developments of new materials are on the anvil and are growing day by day. In this work, two-body abrasive wear test with different loads and abrading distances were performed at room temperature by using a pin on a disk apparatus to...
متن کاملDRY SLIDING WEAR BEHAVIOUR OF STIR CAST LM 25/ZrO2 METAL MATRIX COMPOSITES
In the present study, an investigation into wear properties has been carried out to identify the influence of ZrO2 as the reinforcement material on the LM25 MMC composite. Aluminum LM25 is selected as the base material, and it is reinforced with varying proportions of 0, 3, 6, 9, 12 and 15% of zirconia (ZrO2) manufactured by stir casting. Six tensile test and wear test samples were prepared acc...
متن کاملEffect of Micro Glass Flake on Morphological and Rheological Behaviour of Epoxy Vinyl Ester Composite Coatings
In the present work, attempts were made to investigate the reinforcement and treatment effect of GF on morphological and rheological behaviour of GF/epoxy vinyl ester composites. GF was incorporated into epoxy vinyl ester resin by sonication, and mechanical agitation. Rheological and morphological properties were studied as a function of particle treatment and size distributions. The dispersion...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 5 شماره Issue 2, pp. 121-236
صفحات 138- 146
تاریخ انتشار 2017-04-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023