Preparation of PMMA/MWNTs Nanocomposite Microcellular Foams by In-situ Generation of Supercritical Carbon Dioxide
نویسندگان
چکیده مقاله:
Nanocomposites containing poly(methyl methacrylate) (PMMA) and surface functionalized Multi-Walled Carbon Nanotubes (MWNTs) were synthesized. The dispersion of MWNTs in PMMA was characterized using Transmission Electron Microscopy (TEM).The synthesized nanocomposites were successfully foamed using a simple method based on the in-situ generation of supercritical carbon dioxide (CO2). This method in contrast with conventional methods exempted from high-pressure pump and separated CO2 tank. The effect of MWNTs concentration, saturation temperature and saturation pressure on cellular morphology of the prepared microcellular foams were studied by Scanning Electron Microscopy (SEM), and average cell size and cell density of the prepared foams were studied by image analysis. An increase in cell density, as well as a reduction of cell size, was observed with an increase in the concentration of carbon nanotubes. It was also observed that an elevation of saturation temperature from 90 °C to 100 °C, at constant saturation pressure, leads to a higher cell density and a lower average cell size. Furthermore, an increase in saturation pressure results in a decrease in average cell diameter as well as an increase in cell density. However, the effects of MWNTs concentration on both of average cell size and cell density were proved to be more striking than those of saturation pressure.
منابع مشابه
Tensile and Morphological Properties of Microcellular Polymeric Nanocomposite Foams Reinforced with Multi-walled Carbon Nanotubes
Polyamide 6 (PA6) is used in many applications due to its advantages and improving its properties seems essential. For this purpose in the present study, PA6 was melt compounded with various multi-walled carbon nanotubes (MWCNTs) contents and then was foamed using Azodi carbon amide (ACA) as blowing agent under different injection molding conditions. Morphological properties were investigated u...
متن کاملSupercritical carbon dioxide processed resorbable polymer nanocomposite bone graft substitutes.
The development of synthetic bone graft substitutes is an intense area of research due to the complications associated with the harvest of autogenous bone and concerns about the supply of allogenic bone. Porous resorbable polymers have been used extensively in hard tissue engineering applications, but currently lack load-bearing capacity. Supercritical carbon dioxide (scCO(2)) processing is use...
متن کاملMeasurement and Modeling of Acridine Solubility in Supercritical Carbon Dioxide
Supercritical carbon dioxide has gained increasing attention in food and pharmaceutical processing owing to the fact that it is environmentally inexpensive, not flammable, essentially non-toxic, and it has a convenient critical point. Also, it has been attracting much attention in many fields, such as extraction of sensitive materials and pharmaceutical processing and polymerization processes. ...
متن کاملتأثیر نانولوله‌های کربنی بر مورفولوژی سلولی فوم‌های نانوکامپوزیتی میکروسلولار PC/EPDM
This research aimed at producing microcellular foams (with cell size of 1-10 μm and cell density above 10 9 cell/cm3) from PC/EPDM in order to use in medical devices. Due to the weak nucleation behavior of microcellular polycarbonate foams, it is difficult to prepare them. This research provides valuable information regarding the possibility of making microcellular foams from this polymer by u...
متن کاملSynthesis of polyvinyl pyridine/C60 conjugates in supercritical carbon dioxide*
In the present investigation efforts have been made to synthesis polyvinyl pyridine (PvPy) /C60 conjugates through 2, 2-azobisisobutyronitrile (AIBN) initiated insitu polymerization of PvPy in scCO2.The process of synthesis was monitored under different reaction conditions ranging 1200-1800psi, 60-90 oC over 6 hours. The progress of polymerization was monitored rheoviscometrically. The concentr...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 35 شماره 2
صفحات 63- 72
تاریخ انتشار 2016-04-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023