Morphology control of clay-mineral particles as supports for metallocene catalysts in propylene polymerization
نویسندگان
چکیده مقاله:
Spray dry granulation of clay minerals was studied to obtain clay mineral base support material for metallocene supported olefin polymerization catalysts. The morphology of the granules was strongly influenced by the nature of the clay mineral itself. Because of swelling characteristics of montmorillonite, its water dispersion was highly viscous even in the low slurry concentration (< 4 wt %). Therefore, it was very difficult to control the granule characteristics such as size, shape, and inside structure by the spray dry with the clay mineral slurry. Then we examined some methods in order to change the clay mineral surface properties for getting less viscous dispersion. It was found that the milling of montmorillonite increased the amount of surface OH groups. This surface characteristic change should promote the interaction between the edges and basal planes of the primary particles of milled montmorillonite, resulting in the lowering the slurry viscosity. The milling is effective for overcoming difficulty in use of high concentration montmorillonite slurry in spray dry granulation which is indispensable for producing granules in the wide range of size (10–50 μm). The spray-dried montmorillonite granules are useful as a "Support-Activator" for an olefin polymerization catalyst combined with metallocenes.
منابع مشابه
IN SITU SILICA SUPPORTED METALLOCENE CATALYSTS FOR ETHYLENE POLYMERIZATION
Bis(2-R-ind)ZrCl2 (R: H or phenyl) was supported on different types of silica by in situ impregnation method and used for ethylene polymerization. In this method, the step of catalyst loading on support was eliminated and common alkyl aluminum (triisobutylaluminum, TiBA) cocatalyst was used instead of expensive methyl aluminiumoxane (MAO) cocatalyst in the polymerization. The effect of surface ...
متن کاملEndowing aspecific, unbridged-metallocene propylene-polymerization catalysts with isospecificity: the unprecedented role of MAO.
متن کامل
in situ silica supported metallocene catalysts for ethylene polymerization
bis(2-r-ind)zrcl2 (r: h or phenyl) was supported on different types of silica by in situ impregnation method and used for ethylene polymerization. in this method, the step of catalyst loading on support was eliminated and common alkyl aluminum (triisobutylaluminum, tiba) cocatalyst was used instead of expensive methyl aluminiumoxane (mao) cocatalyst in the polymerization. the effect of surface ...
متن کاملPolymerization of propylene in a minireactor: Effect of polymerization conditions on particle morphology
Gas phase polymerization of propylene was carried out in a semi-batch minireactor using a commercially supported Ziegler–Natta (ZN) catalyst. The influence of variables including monomer partial pressure, external electron donor, reaction temperature and time on the particle morphology and size distribution was investigated. Generally, more uniform fragmentation and particle densities were obta...
متن کاملZiegler-Natta catalysts for propylene polymerization – Interaction of an external donor with the catalyst
The interaction of the external donor (propyltrimethoxysilane - PTMS) with titanium-magnesium catalysts (TMCs) containing dibutylphthalate (DBP) as internal donor, which were prepared in different ways, was studied by chemical analysis and infrared diffuse reflectance spectroscopy (DRIFTS). The chemical composition of the catalysts after their interaction with heptane solutions of PTMS, PTMS/Al...
متن کاملCyclopentadienyl titanium hydroxylaminato complexes as highly active catalysts for the polymerization of propylene.
Half sandwich complexes of titanium bearing eta1 or eta2 bound nitroxide ligands are highly active catalysts for the polymerisation of propylene to high molecular weight atactic poly(propylene).
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 3 شماره 2
صفحات 79- 92
تاریخ انتشار 2016-06-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023